1) autoclaved lightweight concrete waste
压蒸轻质硅酸盐板材废渣
2) light weight silicates aggregate
轻质硅酸盐集料
3) autoclaved silicate products
蒸压硅酸盐制品
1.
In This paper, the influence of the cinder composition and the ratio between Ca, Si and Al in raw materials on the autoclaved silicate products performance has been studied .
结果表明,炉渣的玻璃相含量、活性SiO2、Al2O3总量高于粉煤灰,其蒸压硅酸盐制品强度高于粉煤灰;使用活性SiO2、Al2O3总量较少,SiO2／Al2O3值较低的炉渣需加入较多的砂粉,增大其配料中的硅铝比,以提高其蒸压制品强度。
4) LIGHT BOARD
轻质板材
5) autoclaved silicate concrete
蒸压硅酸盐混凝土
1.
The concept and definition of relative crystallinity of hydrates in autoclaved silicate concrete are put forward according to the fact that the crystallinity of the hydrates is related to their specific surface area.
根据水化产物的结晶程度与其比表面大小有关的事实,提出了用比表面反映水化产物的相对结晶度的概念和定义,采用多元线性回归分析方法探讨了水化产物总量、游离Ca(OH)2、水化产物相对结晶度以及孔结构与蒸压硅酸盐混凝土材料的抗压强度、断裂能和碳化深度的定量关系式。
6) lightweight industrial waste slag
轻质工业废渣
1.
Conclusions were as follows: lightweight industrial waste slag C can be prepared the shotcrete with compressiv
通过对轻质喷射混凝土的研究,得到如下结论:使用轻质工业废渣C可配制1900级的喷射混凝土,其28d抗压强度达到28。
补充资料：轻质硅酸盐集料
分子式：
CAS号：
性质：一种不能水溶的硅酸盐膨胀集料。典型成分为无水硅酸钠，其中氧化钠比二氧化硅为1:2.36。另加入氧化钡，使用时向集料中加入固化剂（硼酸、氯化硼或硼酸钠），再加入水即发生水合作用并固化。碾碎后快速加热到510～540℃使其膨胀。密度为20.8～27.2kg/m3。为优良的轻质制品。
CAS号：
性质：一种不能水溶的硅酸盐膨胀集料。典型成分为无水硅酸钠，其中氧化钠比二氧化硅为1:2.36。另加入氧化钡，使用时向集料中加入固化剂（硼酸、氯化硼或硼酸钠），再加入水即发生水合作用并固化。碾碎后快速加热到510～540℃使其膨胀。密度为20.8～27.2kg/m3。为优良的轻质制品。