1) V-type PTC materials
V型PTC材料
2) V-PTC materials
V-PTC材料
3) V type positive temperature coefficient
V型PTC
4) PTC materials
PTC材料
1.
Improvement in Electrical Stability of CB/HDPE PTC Materials by Chemical Grafted;
化学接枝法提高CB/HDPE PTC材料的稳定性研究
2.
Development of Sr-system PTC materials of low-temperature sintering;
低温烧结锶系PTC材料的研制
3.
At present the preparation of high-Curie temperature PTC materials mostly use lead-substance to move the Curie temperature,which seriously pollutes environment.
为实现电子产品无铅化要求,掺杂预先合成的BNT和其它添加剂,制备出居里温度高于130℃的钛酸钡基无铅PTC材料。
5) PTC material
PTC材料
1.
Research on PTC current limiting characters and fault current protection scheme based on PTC material;
基于PTC材料的短路限流保护方案及PTC限流特性研究
2.
PTC materials, of which room temperature resistivity 140 ?·cm, Curie point 74℃, resistance-temperature coefficient 13.
采用液相施主掺杂和高钙添加相结合的方法,制得性能优良,适合程控电话交换机防雷击、防过流用的耐强电限流器件的PTC材料。
补充资料：1:5型稀土钴永磁材料
分子式：
CAS号：
性质： 稀土(RE)-Co 1:5(原子比)型化合物为：SmCo5，(Sm，Pr)Co5、(Ce、Sm)(Co，Cu、Fe)5～6、MMCo5(MM代表混合轻稀土金属)等为第一代永磁体。其商品磁能积达到127～183kJ/m3(16～23MG3Oe)矫顽力(mHc)1194～3184kA/m(15～40kOe)。代表组成：Co66%(质量)，Sm34%(质量)。用粉末冶金、还原扩散、熔体快淬，铸造等方法制备。这些磁体可制备各种电机、电动机、磁浮选机及核磁共振仪等。
CAS号：
性质： 稀土(RE)-Co 1:5(原子比)型化合物为：SmCo5，(Sm，Pr)Co5、(Ce、Sm)(Co，Cu、Fe)5～6、MMCo5(MM代表混合轻稀土金属)等为第一代永磁体。其商品磁能积达到127～183kJ/m3(16～23MG3Oe)矫顽力(mHc)1194～3184kA/m(15～40kOe)。代表组成：Co66%(质量)，Sm34%(质量)。用粉末冶金、还原扩散、熔体快淬，铸造等方法制备。这些磁体可制备各种电机、电动机、磁浮选机及核磁共振仪等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。