3) copper and aluminum
铜铝
1.
Spot market, futures market is the advanced form of development, China\'s copper and aluminum futures market now has a certain size, has been basically on the spot market with risk aversion and the price discovery function.
铜铝是不可再生资源,是工业生产的重要战略物资,是国民经济发展的基础材料。
4) Cu-Al-Cu
铜铝铜
1.
Optimization of Technological Conditions of Solidphase Rolling of Cu-Al-Cu Bimetallic Composite Materials;
固相轧结铜铝铜双金属复合材料工艺条件优化
5) Cu-Al-Al_2O_3
铜-铝-氧化铝
1.
Preparation and Performance of Cu-Al-Al_2O_3 Porous Materials
铜-铝-氧化铝复合多孔材料的制备及性能
6) copper-aluminum alloy
铜铝合金
1.
The copper-aluminum alloy was prepared by infiltration with the methods of copper powder compact wrapped by aluminum sheet and embed in aluminum powder.
采用铝片包裹和铝粉包埋铜粉压块的方法,通过熔渗制备铜铝合金,铝片包裹法在真空、空气及氩气气氛下进行实验,铝粉包埋法在氩气气氛下进行实验,温度为750℃,保温6h。
补充资料：铜-铝-镍形状记忆合金
分子式：
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。