1) calcined layered double hydroxide
双金属复合氧化物
1.
The XRD patterns of different calcined layered double hydroxides(CLDH) and their ultraviolet absorbing and screening properties have been investigated.
双金属复合氧化物（ＣＬＤＨ）是一类发展迅速的无机层状材料的煅烧产物，在催化、吸附等领域已获长足进展［１］，但作为紫外阻隔材料的性能研究尚鲜见报道。
2) mixed metal oxide
复合金属氧化物
1.
Research on mixed metal oxide catalyst for NO_x removing;
复合金属氧化物选择性催化还原NO_x的研究
2.
Study on preparation and structure of CuO-ZnO-Al_2O_3 mixed metal oxides;
新型CuO-ZnO-Al_2O_3复合金属氧化物的制备及其结构研究
3) mixed metal oxides
复合金属氧化物
1.
This paper introduced the preparations,properties and applied situation of a few catalysts for catalytic removal of nitrogen oxide,which were mixed metal oxides, zeolites, coated noble metals and hydrotalcite like compounds(HTLcs).
综述了催化消除NOx 的几种催化剂———复合金属氧化物、分子筛催化剂、负载型贵金属及类水滑石化合物的制备、特性及应用现状 ,并着重叙述了类水滑石化合物作为催化剂以及催化剂前驱体对氮氧化物消除 (DeNOx)的催化性能及应
2.
In order to realize the application of layered double hydroxides (LDHs) and mixed metal oxides (MMO) in waste water treatment, preparation and oriented assembly of LDHs and MMO nanoparticles have been investigated, and the capacities and mechanisms of removing sulfide anions (S~(2-)) and methyl orange (MO) have been systematically investigated.
本论文从废水处理的角度出发，研究了层状复合金属氢氧化物(Layered double hydroxides，简写为LDHs)及复合金属氧化物(MixedMetal Oxides，简写为MMO)纳米粒子的制备及有序组装，并将其用于以S~(2-)为代表的无机阴离子污染物和以甲基橙(Methyl Orange，简写为MO)为代表的有机阴离子污染物的去除，考察了反应物的结构与去除性能的关系，对去除机理进行了系统而深入的研究。
3.
The system of mixed metal oxides,La2-xSrxCuO4 and La2-xSrxNiO4,supported on a certain kind of mullite particles with size of 28~50 mesh, are prepared with citric acid method, and are characterized by means of XRD and SEM.
本文采用28～50mesh的莫来石颗粒为载体，以柠檬酸盐法制备了一系列负载型La_(2-x)Sr_xCuO_4和La_(2-x)Sr_xCuO_4复合金属氧化物催化剂，XRD和SEM表征了它们的结构，并在CO氧化和N_2O分解的反应中进行了活性和动力学的研究。
4) complex metal oxides
复合金属氧化物
1.
Preparation and characterization of NiFe complex metal oxides;
镍铁复合金属氧化物的制备与表征
5) composite metal oxide
复合金属氧化物
1.
The results indicated that calcination of intercalated LDHs samples could give rise to the formation of composite metal oxides containing Ti and Mo,and calcination temperature had a significant effect on the composite a.
研究发现,MoO42--LDHs在500℃焙烧,产物在丙烯环氧化反应中具有较高的催化活性,这与形成一定结合形式和组成的多元复合金属氧化物有关。
2.
The copper-based multi-composite metal oxides was obtained derived from hydrotalcite prepared by separate nucleation and aging steps,and the structure,morphology,reducibility and catalytic property of this composite were furtherly studied.
本论文针对目前水滑石制备的单一性,尝试采用一系列新的合成方法制备了水滑石层状材料,我们对其制备条件及形成历程进行了探索;以成核晶化隔离法合成的水滑石前体通过高温焙烧得到了铜基多元复合金属氧化物,并对其结构、形貌、还原性能、催化1,4-环己烷二甲酸二甲酯的加氢性能进行了研究。
3.
Different species of composite metal oxide were prepared by various methods.
复合金属氧化物作为一种新型电极材料,不仅具有优良的电容特性,而且能够实现材料性能和成本的合理平衡。
6) Mixed Metal Oxide Catalysts
复合金属氧化物
1.
The Progress and Prospect in Reserch of Isobutene’s Selective Oxidation by Mixed Metal Oxide Catalysts;
复合金属氧化物催化剂上异丁烷的选择氧化的研究
2.
The MoVTeNbOx mixed metal oxide catalysts are considered to be the best catalysts in this catalytic reaction.
MoVTeNbOx复合金属氧化物催化剂被认为是目前对于该反应催化性能最好的一类催化剂。
补充资料：金属复合氧化物
分子式：
CAS号：
性质： 两种以上金属(包括有两种以上氧化态的同种金属)共存的氧化物。它们是O2-以一定方式密堆积，金属阳离子按其离子半径大小充填在O2-组成的合适空隙位置上。在其结构中不存在独立的含氧酸根离子。例如尖晶石型结构：MgAl2O4、MnFe2O4、Zn-CoO4。钙钛矿型结构：CaTiO3、BaTiO3、LiNbO3、SrZrO3等。钛铁矿型结构：FeTiO3。这些结构都不属于含氧酸盐。还有同种金属不同氧化态的混合价态氧化物，如Fe3O4、Pb3O4，它们虽称为铁(II、III)酸铁(III)、铅酸亚铅，实际上不具备含氧阴离子。Fe3O4为反式尖晶石型结构，Pb3O4是由Pb(IV)和Pb(II)和O2-以不同方式结合而成的三维网格结构。金属复合氧化物具有良好的光学、电学、磁学性能，是重要的激光材料、热释电材料、压电材料和强磁性材料等，应用极为广泛。
CAS号：
性质： 两种以上金属(包括有两种以上氧化态的同种金属)共存的氧化物。它们是O2-以一定方式密堆积，金属阳离子按其离子半径大小充填在O2-组成的合适空隙位置上。在其结构中不存在独立的含氧酸根离子。例如尖晶石型结构：MgAl2O4、MnFe2O4、Zn-CoO4。钙钛矿型结构：CaTiO3、BaTiO3、LiNbO3、SrZrO3等。钛铁矿型结构：FeTiO3。这些结构都不属于含氧酸盐。还有同种金属不同氧化态的混合价态氧化物，如Fe3O4、Pb3O4，它们虽称为铁(II、III)酸铁(III)、铅酸亚铅，实际上不具备含氧阴离子。Fe3O4为反式尖晶石型结构，Pb3O4是由Pb(IV)和Pb(II)和O2-以不同方式结合而成的三维网格结构。金属复合氧化物具有良好的光学、电学、磁学性能，是重要的激光材料、热释电材料、压电材料和强磁性材料等，应用极为广泛。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。