1) bound rubber
结合胶
1.
The results showed that when the silica amount was 30 phr,the network did not formed,so the bound rubber could not be measured;the unmodified rubber compounds with 50 phr or 70 phr silica had lower content of bound rubber,and most junctions of network were rigid,so the Pa.
结果表明,白炭黑用量为30份(质量,下同)时网络结构尚未形成,不能测定结合胶;填充了50份和70份的白炭黑复合材料的结合胶含量较低,其网络结构的结点类型以刚性结点为主,混炼胶和硫化胶的Payne效应明显。
2.
Scan electric microphotograph, rubber processing analyzer and bound rubber testing were also applied to further testify the distribution and dispersion of agglomerates, the filler-filler interactions network and the filler-polymer interactions in the rubber matrix, respectivel.
利用DMTA方法研究了分散剂、硅烷偶联剂以及二者并用对二氧化硅增强乙丙橡胶复合材料动态力学性能的影响 ,采用扫描电镜和橡胶加工分析仪测试了填料在橡胶基体中的分散和填料在基体中形成的填料网络结构 ,利用结合胶测试研究了复合材料中填料 橡胶之间的相互作用程度。
3.
The gutta percha rubber filled with various fillers and the bound rubber on the filler surface were investigated by differential scanning calorimetry(DSC) and infra red spectrum(IR).
对混有不同填料的杜仲橡胶及填料界面结合胶进行了差示扫描量热法（ Ｄ Ｓ Ｃ） 分析及红外光谱检测。
2) bound rubber
结合橡胶
1.
Factors affecting reinforcement of high temperature vulcanizates were investigated using(interfacial) bound rubber samples of silicon rubber reinforced by fumed silica nanoparticles with different surface properties.
采用不同表面性质的气相法纳米二氧化硅,利用硅橡胶混炼胶界面结合橡胶来研究高温硫化硅橡胶补强作用的影响因素,并结合扫描电镜分析界面的作用形式。
2.
The results indicate that the changing tendency of the maximum torque and total torque increasing rate is in concordance with the varying rule of bound rubber content, and good agreement with the curve o.
结果表明，其最大扭矩及扭矩积分曲线增加速率的变化趋势与结合橡胶含量的变化规律相一致，并与金属－橡胶粘接体双向剥离比随炭黑的结构性及填充量的依赖曲线具有很好的对应性。
3.
The study begins with the effect of alkaline reagent on the bound rubber; and the modification of method for measuring bound rubber by replacing ammonia with ethylendiamine as alkaline reagent.
研究不同碱性试剂对结合橡胶的影响，并以乙二胺代替氨为碱性试剂对原有结合橡胶测定方法进行改进。
3) tie gum
结合胶层
4) glued joint
胶粘结合
5) glued construction
胶合结构
6) lue binding
胶结合
1.
Hand Lay veneer evaporation process is the use of heating water to produce white plastic glue binding the basic principles to be completed.
手糊薄木工艺是利用加热蒸发水分,使乳白胶产生胶结合作用的基本原理来完成的。
补充资料：结合胶层
分子式：
CAS号：
性质：两种材料或两种胶料，中间用一层橡胶黏结的胶层。例如轮胎胎面胶与帘布层之间的缓冲胶层、橡胶与金属结合时用的硬质胶层结合，都是结合胶层。
CAS号：
性质：两种材料或两种胶料，中间用一层橡胶黏结的胶层。例如轮胎胎面胶与帘布层之间的缓冲胶层、橡胶与金属结合时用的硬质胶层结合，都是结合胶层。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。