1) Anodic polarization behavior
阳极极化行为
1.
In view of preferential corrosion of the titanium alloy welded zone, effect of electron beam welding on anodic polarization behavior of titanium weld metals in acidic CuSO4 solution was studied.
针对钛焊区优先腐蚀问题，研究了电子束扫描焊接对钛合金焊缝金属在酸性硫酸铜溶液中阳极极化行为的影响结果表明，通过改变电子柬扫描频率控制焊缝金属凝固组织形态及尺寸，从而控制了焊缝金属的阳极极化行为找出了焊缝金属与母材相同的阳极极化曲线的最佳匹配；提出了通过控制焊接凝固结晶，使钛合金焊缝金属与母材均等耐腐蚀的新技
2) anode behavior
阳极行为
1.
Effects of additives in the alkaline electrolyte on anode behavior of aluminum;
碱性电解液中的添加剂对铝阳极行为的影响
3) Anodic behavior
阳极行为
1.
The anodic behavior of electrolytic nickel anode in nickel sulfamate plating Solution was investigated,using anodic polarization curves,metallographic observation of cross-sections of nickel deposits,Hull Cell tests with solutions with and without Cl-,F-,bending tests with five solutions of different compositions,and sulfur content analysis in nickel deposit with mass spectrometry.
采用极化曲线、金相观察、赫尔槽电镀试验、弯曲试验和质谱分析方法,研究了氨基磺酸盐镀镍的阳极行为,证明了当在氨基磺酸盐镀液中使用电解镍阳极时,其活化峰值电流和镀液组成有很大的相关性,当镀液中不含F-和Cl-时其阳极活化峰值电流小,阳极处于极化状态,或相当大面积处于极化状态,使氨基磺酸根在极化的阳极表面氧化,从而使含硫化合物夹附于镀镍层,形成镀层内应力,并使镀层成为层状结构,并出现半光亮的外观。
2.
In this paper, anodic behaviors of lead in H2SO4 solution containing an aliphatic amine(HN(C_2H_4NH_2)_2) are studied by measuring anodic polarization curves.
本文以二乙三胺作脂肪胺的代表，通过测量阳极极化曲线研究铅在含二乙三胺的硫酸溶液中的阳极行为的结果表明，在含0。
4) polarization behavior
极化行为
1.
In this paper,polarization behavior of electrodeposition of lead--cadmium and their alloys was studied in thesystem of sulphamate.
本文研究了氨基磺酸盐体系电沉积铅镉及其合金的极化行为,测定了在不同温度、搅拌、添加剂等因素对单金属镀液和混合镀液的极化曲线,表明添加剂间苯二酚对电沉积铅的极化影响较大,可实现铅镉共沉积的目的,初步研究了不同电流对合金镀层成分的影响。
6) anodic polarization
阳极极化
1.
Effect of sulfate ions on anodic polarization behavior of nanocrystalline copper bulk
SO_4~(2-)对块体纳米晶铜阳极极化行为的影响
2.
Kinetic analysis on anodic polarization behavior of nanocrystalline copper in Na_2SO_4 solution
纳米晶铜在Na_2SO_4溶液中阳极极化动力学分析
3.
The electrochemical behavior of AZ31 Mg alloy was investigated by measuring anodic polarization curves and electrochemical impedance spectroscopy(EIS).
采用阳极极化和电化学阻抗谱(EIS)技术研究了AZ31镁合金的电化学腐蚀行为。
补充资料：环状阳极极化曲线
分子式：
CAS号：
性质：钝性金属在含有氯离子的溶液中，用稳态慢速电位扫描方法，先向正电位方向，然后再向负电位方向扫描所测得的呈环状的阳极极化曲线。如图示(图暂缺)。Eb为孔蚀击穿电位，此时钝化膜开始破坏产生孔蚀；Ep为孔蚀保护电位，此时钝化膜重新愈合修补好，金属恢复钝态。这是表征金属对孔蚀敏感性的两个基本电化学参数，可评价金属的孔蚀倾向。
CAS号：
性质：钝性金属在含有氯离子的溶液中，用稳态慢速电位扫描方法，先向正电位方向，然后再向负电位方向扫描所测得的呈环状的阳极极化曲线。如图示(图暂缺)。Eb为孔蚀击穿电位，此时钝化膜开始破坏产生孔蚀；Ep为孔蚀保护电位，此时钝化膜重新愈合修补好，金属恢复钝态。这是表征金属对孔蚀敏感性的两个基本电化学参数，可评价金属的孔蚀倾向。