1) Fe Al P alloys
Fe-Al-P合金
2) Fe-(Al,Ga)-(P,Si,B)amorphous alloys
Fe-(Al,Ga)-(P,Si,B)非晶合金
3) Al-Fe alloy
Al-Fe合金
1.
To investigate the effect of an alternating magnetic field on the morphology and distribution of iron-containing intermetallic phases in Al-Fe alloy,the near eutectic Al-1.
研究了交流磁场对Al-Fe合金中含铁相形态及分布的影响。
2.
In order to solve the problems of the primary Fe-rich phase separating the metal matrix seriously and deteriorating the property of hypereutectic Al-Fe alloy, rare earth (Y) metal was used to modify Al-5%Fe alloy.
针对普通熔铸条件下过共晶Al-Fe合金中初生富铁相严重割裂基体、恶化合金性能的问题,采用稀土元素Y对Al-5%Fe合金进行变质处理。
4) Fe-Al alloy
Fe-Al合金
1.
Positron lifetime measurements have been performed in binary Fe-Al alloys with different compositions and Fe3Al alloys doped with Cr and Si.
对二元Fe-Al合金,含Cr和Si的Fe3Al合金的正电子寿命谱侧量表明:随着二元 Fe-Al合金Al含量的增加,空位浓度增加,微孔洞的开空间增大,在Al含量高于40%(原子分数)的 B2-FeAl合金中存在着较高的空位浓度和开空间相当于Fe中10-15个空位聚集体的微空洞,在B3-FeAl和D03-Fe3Al合金中,晶格中最邻近的Fe－Al原子对之间发生Fe d-Alp杂化作用,Al的3p电子与Fe的3d电子被局域化并形成共价键,导致合金中的自由电子密度降低,二元Fe-Al合金中的平均电子密度随着Al含量的增加而下降,用Cr元素对Fe3Al进行合金化,合金基体和晶界处的自由电子密度均增加;而加入Si元素,合金基体和晶界处的自由电子密度均减小,讨论了Fe-Al合金的微结构对其力学性能的影响。
2.
The microdefect,electron density and the Fe 3d-Al 3p interaction in binary Fe-Al alloys with difference chemical composition have been investigated by positron lifetime spectra and coincidence Doppler broadening spectra of positron annihilation radiation.
采用符合正电子湮没辐射多普勒展宽装置和寿命谱仪研究不同化学成分的二元Fe-Al合金中的微观缺陷、电子密度以及Fe 3d-Al 3p电子的交互作用,合金元素对Fe-Al合金中微观缺陷、电子密度和3d电子的影响。
3.
Aluminum in molten zinc tends to segregate at the Fe:molten zinc interface with eventual precipitation of the Fe-Al alloy that inhibits the development of Fe-Zn compound.
从更微观的角度看,由于缺陷处浸入锌液后生成的Fe-Al合金层比正常部位少,抑制作用减小使该处合金化速度变快,所以缺陷处Zn-Fe合金层生成量大,容易产生条状凸起。
5) Fe-Al alloys
Fe-Al合金
1.
The inverted torsion pendulum technique (JN-1 vacuum internal friction technique) was used to test the damping capacities of Fe-Al alloys.
采用光学显微和扫描电子显微观察(SEM)等方法,系统地研究了Fe-Al系铁磁性阻尼合金的微观组织,考察了合金元素、热处理工艺对合金阻尼性能和力学性能的影响,探讨了Fe-Al合金产生高阻尼特性的微观机制以及Fe-Al系高阻尼合金的同质和异质焊接性能。
2.
The internal depletion behavior of B2 Fe-Al alloys was examined in the paper.
对B2结构Fe-Al合金的内耗特征进行了研究。
3.
It has been well documented that the mechanical and physical properties of Fe-Al alloys are highly sensitive to the atomic defects.
原子缺陷对Fe-Al合金的力学和物理性能有重要影响,而内耗是对原子缺陷运动非常敏感的物理量。
6) Fe-P alloy
Fe-P合金
1.
Study of Fe-P alloy brush plating using soluble anode;
可溶性阳极快速刷镀Fe-P合金的研究
2.
Fe-P alloy was prepared by electroless deposition and the corrosion behavior of electroless Fe-P deposits in 1 mol/L NaOH media was investigated by electrochemical method.
用化学镀的方法制备Fe-P合金,分析化学镀层在1mol/LNaOH介质中的腐蚀行为。
3.
The plating conditions of chemical plating of Fe-P alloy were discussed.
研究了化学镀Fe-P合金中镀液组分和工艺变化对化学沉积速率的影响。
补充资料：Fe3Al基金属间化合物高温合金
Fe3Al基金属间化合物高温合金
Fe_(3)Al-base intermetallic compound superalloy
Fe3AI JIJ一nshujlon huahewu gaowen heJinFe3AI基金属间化合物高温合金(F e3AI一baseintermetallie eomPound suPeralloy)以Fe3AI相为基体的金属间化合物高温合金。该合金具有优异的高温抗氧化、抗硫化腐蚀性能，合金密度较小，因为不含贵重元素，故价格低廉，很适合于在高温氧化、硫化腐蚀的环境中工作。Fe3AI合金有两个不足之处:室温很脆，伸长率仅3%左右;高温强度不足。通过添加合金元素铬、硼，采取温加工工艺和合理的热处理制度，基本上解决了室温脆性问题，室温拉伸伸长率提高到15%左右。提高强度的途径是进行合金化，添加错、妮、铝等元素进行固溶强化和析出第二相进行时效强化，使合金室温拉伸强度达到l000MPa，600℃拉伸强度达到560MPa。Fe3AI基金属间化合物高温合金可以制造加热元件、炉子紧固件、热交换器、汽车用管材、石油管道和磁性元件等。该合金在真正走向实用之前，应在冶炼工艺和热加工工艺方面进行改进。 (}马培立卜
说明：补充资料仅用于学习参考，请勿用于其它任何用途。