1) solution hydrogenation
溶液加氢
1.
The preparation methods of hydrogenated nitrile rubber using nitrile rubber by the copolymerization process,the emulsion hydrogenation process and solution hydrogenation process,and the process conditions,hydrogenation units and the remove of rhodium-containing catalyst residue were reviewed with 52 references.
综述了用共聚合法、乳液加氢法和溶液加氢法制备饱和丁腈橡胶的技术，介绍了工艺条件、加氢设备及残留催化剂铑的脱除。
2) homogeneous solution hydrogenation
溶液均相加氢
1.
The kinetic study of the homogeneous solution hydrogenation of NBR using Rh-Ru bimetallic complex catalyst, has been carried out for the first time.
本文首次以Rh-Ru双金属催化剂对NBR进行溶液均相加氢动力学研究，从加氢动力学数据求得各因素相应的反应级数和加氢速率常数k，导出该催化剂在115℃～145℃对NBR溶液均相加氢速率方程： -d[C=C]／dt=k[C=C]~(1。
3) Liquid phase hydrogenation
液相加氢
1.
Catalytic activity of Ni-B-Mo/Sep catalyst in liquid phase hydrogenation of furfural to furfuralcohol was investigated.
采用正交实验法优化海泡石(记为Sep)的改性条件,包括酸改性时盐酸溶液中HCl的质量分数、酸处理时间和热改性时的焙烧温度、焙烧时间;以改性后的海泡石为载体,采用浸渍和化学还原法制备了Ni-B-Mo/Sep催化剂,以糠醛液相加氢制糠醇为探针反应,考察了Ni-B-Mo/Sep催化剂的性能。
2.
A new Ni catalyst for liquid phase hydrogenation was prepared by impregnation method.
针对工业上通常采用的辛烯醛加氢制备辛醇的工艺,采用浸渍法制备了一种新型镍系液相加氢催化剂。
3.
According to the liquid phase hydrogenation technology in the production of 2-ethylhexanol, we exploited a new series of Ni catalysts for liquid phase hydrogenation.
针对工业上两步法加氢辛醇合成过程中的第二步液相加氢反应工艺，研制开发了新型镍系液相加氢催化剂。
4) liquid-phase hydrogenation
液相加氢
1.
Introduces the catalysts and methods of dehalogenation inhibiting in the preparation of 6-ehloro-3-aminotoluenes-4-sulfonie acid, or CLT acid, by Liquid-phase hydrogenation of 6-chloro-3-nitrotoluene-4-sulfonic acid, and the related process conditions is discussed.
介绍了6-氯-3-硝基甲苯-4-磺酸液相加氢制备6-氯-3-氨基甲苯-4-磺酸，即CLT酸的催化剂及抑制脱氯方法，并讨论了相关的工艺条件。
6) hydrogenation liquefaction
加氢液化
1.
The results of tests for the swelled coals in which the pyridine solvent are driven out completely, such as hydrogenation liquefaction test, coking test under lower temperature for measure tar yield, measure volatile y.
经过对脱除溶剂后溶胀煤的加氢液化实验、低温干馏焦油产率测定、挥发分产率测定及体积溶胀率的测定 ,结果表明该三种原煤具有良好的可溶胀性能 ,溶胀煤均具有良好的加氢液化性能 。
2.
Lignin that came from black liquor of papermaking Industry was used to prepare aromatics and fatty hydrocarbon compounds through hydrogenation liquefaction process.
本文针对我国造纸行业的副产物木质素进行了加氢液化研究。
补充资料：铝酸钠溶液加种子分解
铝酸钠溶液加种子分解
decomposition of sodium aluminate liquor with seed
分解原液息森，，化。竺一七肖创 分解母液 (返回溶出) 图1铝酸钠溶液加种子分解工艺流程在用种子分解高浓度铝酸钠溶液生产砂状氧化铝的工艺中，以瑞士的新瑞铝法最具代表性。该法采用两段分解法:一段分解是用晶粒附聚的条件产出粗颧粒;二段分解是再通过控制晶体生长条件使颗粒强度和产出率增加。晶粒附聚的初温为339~35oK，加种子量按溶液过饱和度(g/L)与细种子表面积(m“/L)之比为7~169/m，计，附聚时间为6h。晶体生长是把物料冷却到3z8K温度后，按4009/L(粗、细粒合计)加入氢氧化铝种子，停留时间为5。~7叭。 氮氧化铝分离和洗涤多在专用的水力旋流器、弧形筛以及多级沉降分级槽进行。中国开发的旋流筛可一次完成成品氢氧化铝、粗晶种和细晶种的分级.晶种氢氧化铝用转鼓过滤机撼去所附带的母液。成品氢氧化铝稠浓浆液采用二次反向过滤洗涤。洗涤后成品氢氧化铝含Na20应不大于0.12%，水分不高于12纬。采用助滤剂可使成品氢氧化铝附着水含量降到6%~8%。设备包括溶液冷却设备、分解槽、分离(分级)和洗涤设备。 冷却设备将铝酸钠溶液冷却到分解初温的设备。采用较多的有板式热交换器和闪速蒸发器组等。板式热交换器是利用分解母液冷却分解原液。闪速蒸发冷却一般采用2一5级闪速蒸发。二次蒸气用于逐级加热蒸发前的分解母液，二次蒸气冷凝水可用于洗涤氢氧化铝。 分解槽组分解槽有空气搅拌和机械搅拌两种形式。操作按组配置，每组12~15台。 (1)空气搅拌分解槽。为焊接封闭容器，内装两个空气升液器，槽容积为1250一lsoom3，直径7.75一9.om，总高25.7一33.sm(图2)。新建分解槽容积达3000一40oom3。 压缩__〕 图2空气搅拌分解槽 1一槽壳;2一过料空气升液器; 3一冷却水套;4一搅拌空气升液器 (2)机械搅拌分解槽。由于这种分解槽能减少动力消耗，在20世纪70年代又重新获得发展。机械搅拌分两种方式，一种是轴流式机械搅拌，在空气搅拌分解槽升液管内的上部装设轴流泵式螺旋桨;另一种是用螺旋桨叶搅拌的平底分解槽。螺旋桨叶形状特殊，槽内壁上装设挡板，以造成强烈搅拌。最大的机械搅拌分解槽的容积为4500m3。在欧洲式拜耳法分解条件下，得到产出率高、粒度细的氢氧化铝。这种氢氧化铝需经1573K温度缎烧，才能制得不易飞扬的“面粉状”氧化铝。在美国式拜耳法分解条件下，得到产出率低、粒度粗的氢氧化铝。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条