1) austempering immedidely after inter critical annealing
临界区等温淬火
1.
Bainite ferrite and retained austenite are obtained through austempering immedidely after inter critical annealing in dual phase steel containing C,Si and Mn.
新型 TRIP复相钢仅含 C、Si、Mn等合金元素 ,采用临界区等温淬火热处理工艺 ,获得铁素体、贝氏体和残余奥氏体三相组织。
2) austempering after intercritical annealing
亚临界等温淬火
3) critical area quenching
临界区淬火
4) critical hardening
临界淬火
5) austempering
[,ɔ:s'tempəriŋ]
等温淬火
1.
Effects of Si and Austempering on the Wearresistance Property of ZG30SiMnCr;
Si及等温淬火工艺对ZG30SiMnCr耐磨性的影响
2.
Effect of Austempering on Mechanical Properties and Abrasion-Resistance of Mn -Cr Alloyed White Cast Iron;
等温淬火对Mn-Cr白口铸铁力学性能和耐磨性的影响
3.
Research of austempering process of low-carbon ductile iron;
低碳球铁的等温淬火工艺研究
6) isothermal hardening
等温淬火
1.
Strengthening and Toughening of Die Steel Cr7Mo3V2Si by Isothermal Hardening with Prenitriding and Diffusion;
模具钢Cr7Mo3V2Si渗扩氮等温淬火复合强韧化
2.
The influences of various isothermal hardening treatments on microstructure and properties of semi-steel made by quenching and isothermal hardening and forging,which contain 1.
研究了空淬、等温淬火及锻热等温淬火对含1。
3.
2)=900～1000 MPa,σ_b=1300～1564 MPa)and excellence plasticity(δ_5=15%～18%)were obtained after aus- tenitization at 840～880℃followed by isothermal hardening for 3 hours.
试验用钢经840～880℃加热,保温20min,在320～360℃的盐浴炉中等温淬火3 h,得到较高的强度(σ_(0。
补充资料：35CrNi3MoV钢等温淬火组织
35CrNi3MoV钢等温淬火组织
35CrNi3MoV钢等温淬火组织马氏体(绿)+见氏体(棕)残余奥氏体(浅黄)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。