1)  heat resistant alloy
高合金
2)  high alloying
高合金化
1.
In this experiment, the two high alloying Al-2 at%Cu-8 at%Mg、Al-3 at%Cu-12 at%Mg alloys were cast in cuneal mould at different cooling rates after the delicate alloy composition design.
通过合金成分设计,采用常规铸造工艺在不同的凝固速度下制备原子比Cu∶Mg=1∶4的Al-2%Cu-8%Mg(原子分数,下同)、Al-3%Cu-12%Mg两种高合金化铝合金,利用XRD、OM、SEM、TEM等分析测试手段,观察了合金的组织特征。
3)  High alloy steels
高合金钢
4)  high alloy steel
高合金钢
1.
photoelectric spectroanalysis for multielement determination of high alloy steel;
高合金钢中的多元素光电光谱测定
2.
Although root over-burn of high alloy steel welding lines is not defined as defect by welding regulations,it significantly affects the life of welded pipes.
高合金钢焊缝根部的"过烧"虽然未被相关焊接规程定义为缺陷,但实际上对焊接管道的使用寿命有极大的影响。
3.
It is serious for embrittlement of high alloy steel carbonitriding and it is difficult to eliminate by low temperature tempering,for example,after quenching and 150℃ 3h tempering,the reductions of area of 20Cr2Ni4A and 18CrNiWA steels in carbonitriding are 10% and 6 4% respectively of those heating in air.
研究了碳氮共渗时的氢脆及其消除方法 ,发现高合金钢氢脆敏感性大 ,在一般低温回火中很难消除 ,如淬火后经 15 0℃×3h回火 ,2 0Cr2Ni4A和 18CrNiWA钢的断面收缩率在碳氮共渗时分别为空气加热的 10 %及 6 4%。
5)  high-alloy steel
高合金钢
6)  high-alloy
高合金的
参考词条
补充资料：高合金钢
分子式：
分子量：
CAS号：

性质：合金元素的总含量一般在10%以上的合金钢。可用于制造使用温度高于600℃的化工设备。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。