1) Zn ferrite
Zn铁氧体
1.
Nanocrystalline Zn ferrite was prepared by high energy ball milling.
用高能球磨法制备了纳米晶Zn铁氧体通过样品的Mossbauer谱及XRD谱的测定，研究了纳米晶的形成过程结果表明：球磨约3hα-Fe2O3即与ZnO发生机械化学反应生成Zn铁氧体，这种反应是通过先形成α-Fe2O3-ZnO固溶体而进行的。
2.
Nanocrystalline Zn ferrite,synthesized by hig h energy ball milling from ZnO+α-Fe2O3 powder mixture,exhibited non-normal spinel structure and ferrimagnetism (σs=16.
通过高能球磨方法由α-Fe2O3+ZnO混合粉体制得的Zn铁氧体纳米晶具有非正型分布的尖晶石结构,表现为亚铁磁性,其比饱和磁化强度σs=16。
2) zinc ferrite
Zn铁氧体
1.
2 K to RT, showing that their magnetic ordering took place at a much higher temperature than that of bulk zinc ferrite.
用固相反应法制备了大块的 Zn Fe2 O4 ,用聚乙烯醇 ( PVA)溶胶凝胶法制备出 6～ 90 nm的 Zn Fe2 O4 纳米微粉 ,用 X衍射研究了 Zn铁氧体纳米颗粒的结构 。
3) Mn-Zn ferrite
Mn-Zn铁氧体
1.
Preparation of Cu doped Mn-Zn ferrite by spent Zn-Mn batteries;
废旧锌锰电池制备Cu掺杂Mn-Zn铁氧体
2.
Mn-Zn ferrite nanocrystalline was prepared by solgel auto-combustion process,and the technics was analyzed by means of TG-DTA, FT-IR and XRD.
用溶胶-凝胶自燃烧法制备了Mn-Zn铁氧体纳米晶体,用TG-DTA,FT-IR和XRD等3种分析方法研究了其制备工艺。
3.
Using spent alkaline Zn-Mn batteries as resource materials through dissolving with nitric acid and tartaric acid as gelata in sol-gel method Mn-Zn ferrite powders with cubic spinel structure are synthesized directly.
以硝酸溶解废旧碱性锌锰电池所得的溶液为原料,以酒石酸为凝胶剂,采用溶胶-凝胶法制备出了具有尖晶石结构的Mn-Zn铁氧体。
4) Ni-Zn ferrite
Ni-Zn铁氧体
1.
Formation of nanocrystalline spinel Ni-Zn ferrite by mechanical alloying;
用机械合金化方法制备纳米晶Ni-Zn铁氧体
2.
Domain wall motion research in Ni-Zn ferrite under constant rate of H ;
匀速加场下Ni-Zn铁氧体DW运动的描述
3.
Effect of doping the different rare-earth oxide on wave absorbability of Ni-Zn ferrite/Al-alloy foams materials
掺杂不同稀土氧化物对Ni-Zn铁氧体/泡沫铝材料吸波性能的影响
5) Mn-Zn ferrites
Mn-Zn铁氧体
1.
The effect of doped nano-SiO_2 and CaCO_3 on the power loss of Mn-Zn ferrites was investigated,and scanning electron microscopy was used to analyze the microstructure,grain boundary and elements distribution of Mn-Zn ferrites.
对添加纳米级SiO2和普通级CaCO3组合对Mn-Zn铁氧体功率损耗的影响进行研究,采用扫描电子显微镜对Mn-Zn铁氧体材料的显微结构、晶界以及元素分布进行观察分析。
2.
DC superposition characteristic of permeability of Mn-Zn ferrites was researched in this paper.
对Mn-Zn铁氧体磁芯磁导率的直流叠加特性进行了研究。
6) Li-Zn ferrite
Li-Zn铁氧体
补充资料：ACTH-Zn
分子式：
CAS号：
性质：又称氢氧化锌促皮质素，长效促皮质素。由精制促皮质素吸附氢氧化锌而得的悬浮液，pH值7～8。于2～10℃贮存可保持活性两年以上。因含有结合的氢氧化锌，能抑制体内蛋白酶对促皮质素的水解，显著减慢人体内对促皮质素的吸收速度，而具有延效作用。见促皮质素。
CAS号：
性质：又称氢氧化锌促皮质素，长效促皮质素。由精制促皮质素吸附氢氧化锌而得的悬浮液，pH值7～8。于2～10℃贮存可保持活性两年以上。因含有结合的氢氧化锌，能抑制体内蛋白酶对促皮质素的水解，显著减慢人体内对促皮质素的吸收速度，而具有延效作用。见促皮质素。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条