1) nitrogen partial pressure
氮气分压
1.
The crystal structure and mechanical properties of (Ti,Al)N films are strongly dependent on the nitrogen partial pressure The st.
试验结果表明，采用Ti，Al原子比为1∶1的靶材在不同的氮气分压下制成的样品薄膜在硬度方面有差异，在氮气分压为1。
2.
It was found that the nitrogen partial pressure and substrate temperature are thetwo important factors affecting the formation of Fe-N phases and their magneticproperties.
系统研究了氮气分压、基底温度，溅射功率等制备工艺条件对 Fe-N 薄膜结构和磁性的影响，以及 Fe-N 薄膜的饱和磁化强度的尺寸效应。
2) synthesis conversion
最低氮气分压
3) N2-pressurized
氮气加压
4) compressed Nitrogen
压缩氮气
5) nitrogen pressure
氮气压力
1.
Polyphase Y-α/β-Sialon powders were prepared by SHS method, with St, Al, Y2O3 and Si3N4as raw materials under high nitrogen pressure.
本文通过组成设计，以Si、Al、Y2O3为原料，Si3N4为稀释剂，利用自蔓延高温合成法（SHS）制备了Y－α／β－Sialon粉末；并利用XRD、化学分析法分别研究了α－Sialon简称α′）、β－Sialon简称β′）相组成和游离硅含量；且详细讨论了氮气压力、稀释剂含量对生成物Y－α／β－Sialon中的α′、β′相及残余硅含量的影响。
2.
The effect of Y-TZP (3mol% Y2O3) and nitrogen pressure on the sintering properties,phase composition, microstructure and mechanical properties of GPS Si3N4 Ceramic Materials with Y2O3 and Al2O3 as sintering aids were studied.
本文研究了Ｙ－ＴＺＰ（３ｍｏｌ％Ｙ２Ｏ３）和氮气压力对ＧＰＳＳｉ３Ｎ４陶瓷材料的烧结性能和力学性能、相组成及微观结构的影响，添加５ｗｔ％、１０ｗｔ％、１５ｗｔ％、２０ｗｔ％Ｙ－ＴＺＰ的氨化硅复合材料在１７７０～１８００℃，氮气压力分别为１ＭＰａ、２ＭＰａ、３ＭＰａ下烧成，获得相对密度＞９５％的烧结体。
6) low nitrogen pressure
低氮气压
1.
Self-propagating High-temperature Synthesis(SHS)of Si 3N 4/SiC composite powder from silicon and carbon powder under low nitrogen pressure has been investigated,it is feasible to synthesize the composite powder in-situ under nitrogen pressure 0 5～0 6?MPa.
探讨了硅粉与碳粉混合料在 0 5～ 0 6MPa的低氮气压下自蔓延高温合成 (SHS)的可行性 ,起始原料中加入适量的Si3N4作稀释剂 ,可促进Si粉向Si3N4转变。
补充资料：电容分压器(见分压器)
电容分压器(见分压器)
capacitor voltage dividers
d)onf。日g无en丫oq{电容分压器(eaPaeitor voltage dividers)见分压器。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。