1) Polymeric aluminum magnesian silicates-ulfate (PAMSS)
聚硅硫酸铝镁(PAMSS)
2) polymeric aluminum magnesian's ilicate-sulfate(PAMSS)
聚合硅酸硫酸铝镁(PAMSS)
3) polysilicic acid containing aluminum sulfate and magnesium sulfate
聚硅酸硫酸铝镁
4) Polysilicate containing aluminum and magnesium
聚硅酸铝镁
5) polysilicate aluminium sulphate
聚硅硫酸铝
1.
The stable polysilicate aluminium sulphate(PASS) with high aluminium content was prepared by composite method with the addition of stabilizer,using Na2SiO3·9H2O,Al2(SO4)3·18H2O as raw materials.
18H2O为原料,加入一定量稳定剂,采用复合法制备出高铝含量且稳定的聚硅硫酸铝(PASS)。
6) polysilicate ferric aluminum sulfate
聚硅酸硫酸铁铝
1.
The effect of pH,settling time,dosage and molar ratio on polysilicate ferric aluminum sulfate(PSFAS) for disposal of arsenic wastewater is investigated.
以电厂中的含砷废水为研究对象,考察了pH值、沉降时间、投加量、铁铝硅摩尔比对聚硅酸硫酸铁铝混凝处理含砷废水的影响。
补充资料:铝硅镁铸造合金
分子式:
CAS号:
性质:由铝、镁、硅为主成分的铸造合金。含硅一般在12%以下,同时加入少量铜和镍以增加强度、细化晶粒和使组织稳定化。杨氏模量71.0GPa,冲击值0.74~1.1J,疲劳极限50~80MPa。采用固溶、时效处理和淬火热处理方法制造。用于泵铸造件、支架等。