1) dynamic crack propagation speed
动态裂纹扩展速度
2) crack propagation rate
裂纹扩展速度
1.
The CF crack propagation rate (in platform region) of martensitic GC-4 steel ismuch higher than that of bainitic one.
5%NaCl溶液中的CF裂纹扩展曲线上,都出现了类似于应力腐蚀的平台区,而且马氏体组织GC-4钢的平台区裂纹扩展速度远大于贝氏体组织。
2.
As the isothermal temperature was changed from 190℃ to 300℃, the SCC crack propagation rate (da/dt)_Ⅱ decreased by one order of magnitude.
5％NaCl溶液中,其应力强度因子门槛值K_(ISCC)没有显著差别,但其应力腐蚀裂纹扩展速度相关较大,随等温温度的升高,应力腐蚀裂纹扩展速度大大降低。
3) crack propagation velocity
裂纹扩展速度
1.
according to the theories of dynamic mechanics and fracture mechanics,we work out the rational impact split thickness by fracture criterion and the studing of crack propagation velocity.
根据动力学及断裂力学的有关理论,对煤体断裂准则及裂纹扩展速度进行了研究,确定了合理的冲劈厚
2.
The fastest crack propagation velocity for Mg-3.
结果表明:在高速冲击条件下,单相Mg-L i合金的裂纹扩展主要是减速过程,且随L i含量增加,由于合金组织结构的转变(hcp→bcc),加之合金中A l的添加而沉淀的MgL i2A l与A lL i粒子的作用,致使Mg-L i合金的裂纹扩展速度显著降低。
3.
The dynamic fracture toughness, crack propagation velocity and arrest toughness of materials were simultaneously obtained with this method.
本文利用Hopkinson单压杆实验装置 ,对材料的弹塑性动态断裂特性进行了研究 ,建立了应力波载荷作用下动态裂纹起裂、扩展、止裂全过程的动态分析方法 ,采用该方法可同时测得材料的动态断裂韧性、裂纹扩展速度和止裂韧性。
4) fracture speed
裂纹扩展的速度
5) crack dynamic propagation
裂纹动态扩展
1.
Based on the theory of complex functions,anti-plane problems on crack dynamic propagation under the action of variable loads Pt,Pt/x are studied respectively.
通过复变函数论的方法,对变载荷P t、P t/x作用下裂纹动态扩展的反平面问题分别进行研究。
补充资料：裂纹失稳扩展
分子式：
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。