1) conventional sulfur curing system
常硫硫化体系
1.
The results showed that comparing conventional sulfur curing system with sulfurless curing system the former exhibited slightly shorter scorch time and longer optimum cure time and better mechanical property,but its heat age stability was worse.
结果表明 :常硫硫化体系与无硫硫化体系相比 ,前者胶料的焦烧时间稍短 ,正硫化时间稍长 ;常硫硫化体系胶料的力学性能比无硫硫化体系胶料好 ,但无硫硫化体系胶料的耐热老化性能比常硫硫化体系胶料要好。
2) vulcanization system
硫化体系
1.
Effect of vulcanization time and vulcanization system on thermal ageing property of clay-rubber masterbatch;
硫化时间及硫化体系对粘土胶热氧老化性能的影响
2.
With regard to mechanical properties,heat resistance,fuel resistance and shelf life of ECO-compounds as well as material cost,the lead free and ETU free vulcanization system for ECO was developed and improved by means of comb.
由于健康和环境方面的原因,在欧洲,氯醚橡胶是不允许使用含铅和乙基硫脲的硫化体系的。
3.
Carboxylated nitrile rubber (XNBR) were vulcanizated with sulphur-free vulcanization system,low-sulphur high-accelerant vulcanization system, general sulphur vulcanization system,peroxide vulcanization system,metal oxide vulcanization system and sulphur/metal oxide vulcanization system.
用无硫硫化体系、低硫高促进剂硫化体系、普通硫黄硫化体系、过氧化物硫化体系、金属氧化物硫化体系和硫黄/金属氧化物硫化体系对羧基丁腈橡胶(XNBR)进行了硫化,研究了XNBR的硫化性能、物理机械性能、耐老化性能、压缩永久变形和耐油性能。
3) curing system
硫化体系
1.
Effect of blowing agent and curing system on properties of NR/SBR foam;
发泡剂和硫化体系对NR/SBR并用海绵胶性能的影响
2.
Study on curing system of NR/BR/TPI blend;
NR/BR/TPI共混物硫化体系的研究
3.
Study on curing systems of NR/TPI blends;
天然橡胶/反式-1,4-聚异戊二烯并用胶硫化体系的研究
4) thiourea curing system
硫脲硫化体系
1.
Recipe optimization of thiourea curing system for chlorinated polyethylene;
氯化聚乙烯硫脲硫化体系配方优化
5) sulfur curing system
硫黄硫化体系
1.
Optimized design of sulfur curing system for EPDM;
EPDM硫黄硫化体系的优化设计
2.
The influence of the sulfur curing system and the blending ratio of IIR/EPDM on the physical properties of blend was investigated.
研究IIR/EPDM体系中共混比、硫黄硫化体系对其共混胶性能的影响。
6) sulfurless curing system
无硫硫化体系
1.
The results showed that comparing conventional sulfur curing system with sulfurless curing system the former exhibited slightly shorter scorch time and longer optimum cure time and better mechanical property,but its heat age stability was worse.
结果表明 :常硫硫化体系与无硫硫化体系相比 ,前者胶料的焦烧时间稍短 ,正硫化时间稍长 ;常硫硫化体系胶料的力学性能比无硫硫化体系胶料好 ,但无硫硫化体系胶料的耐热老化性能比常硫硫化体系胶料要好。
补充资料：无硫硫化
分子式：
CAS号：
性质：在橡胶胶料配方中未应用硫黄进行交联称无硫硫化胶料，又称非硫硫化。对饱和型橡胶不能采用硫黄体系硫化，必须采用非硫硫化体系。对不饱和型橡胶，为改善硫化胶性能也有的采用非硫硫化法。目前常用的非硫硫化体系硫化剂，有金属氧化物、有机过氧化物、树脂、醌肟化合物、多元胺等。还有离子型交联、异氰酸酯反应交联和辐射交联等。
CAS号：
性质：在橡胶胶料配方中未应用硫黄进行交联称无硫硫化胶料，又称非硫硫化。对饱和型橡胶不能采用硫黄体系硫化，必须采用非硫硫化体系。对不饱和型橡胶，为改善硫化胶性能也有的采用非硫硫化法。目前常用的非硫硫化体系硫化剂，有金属氧化物、有机过氧化物、树脂、醌肟化合物、多元胺等。还有离子型交联、异氰酸酯反应交联和辐射交联等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。