1) vulcanization curve
硫化曲线
1.
The vulcanization curves of EPDM were determined by Monsanto rheometer at 180℃,170℃,160℃,150℃ and 140℃.
用孟山都流变仪测定了三元乙丙橡胶在１８０，１７０，１６０，１５０，１４０℃下的硫化曲线。
2.
The vulcanization curves of three kinds of nitrile rubber in different vulcanization systems were determined by Monsanto rheometer at 170 ℃.
用孟山都流变仪测定了1种NBR—18硫化体系和2种NSR—26硫化体系在170℃下的硫化曲线,三者的转矩P均随硫化时间t的增加而增大。
2) reversion percentage curve
硫化返原率曲线
1.
Characterizing anti-reversion of rubber compound with reversion percentage curve;
用硫化返原率曲线表征胶料的抗硫化返原性能
3) Linearigation of's calibration curve
硫工作曲线直化
4) polarization curve
极化曲线
1.
Segmentation identification algorithm for fuel cell polarization curve
燃料电池极化曲线分段辨识算法
2.
The corrosion inhibition performance of six inhibitors on 316L stainless steel in simulated cooling water is studied by polarization curves,AC impedance,and Mott-Schottky plots.
采用极化曲线、Mott-Schottky图和交流阻抗谱研究了不同缓蚀剂对316L不锈钢的缓蚀效果。
3.
The role of corrosion with or without cavitation was analyzed by the measurements of polarization curve.
测量了静态和空蚀条件下涂层的极化曲线,比较了常态和阴极保护下空蚀时的腐蚀电流变化,通过分析涂层在静态、空蚀以及阴极保护下空蚀的交流阻抗谱(EIS),进一步探讨了空蚀机理。
5) polarization
[英][,pəulərai'zeiʃən] [美][,polərə'zeʃən]
极化曲线
1.
The bacteria in seawater were cultured in batch and the corrosion behavior of 304 stainless steel in the medium of marine microorganisms was investigated by polarization curves and electrochemical impedance spectroscopy, etc.
利用间歇式方法培养海水中的细菌,用极化曲线和电化学阻抗谱研究304不锈钢在有菌和无菌培养基中的腐蚀行为。
2.
SEM,XPS and polarization are used to study the oxide film formed on zinc surface.
表面分析和 Tafel极化曲线结果表明 :Zn获得缓蚀作用是由于在其表面形成含铈的氢氧化物和 Ce O2 的复合膜。
6) polarization curves
极化曲线
1.
Application of polarization curves in chlor-alkali industry
极化曲线在氯碱工业的应用
2.
15%,polarization curves represented anodic dissolution process;when the concentration was above 0.
10%时,极化曲线呈现阳极活化溶解过程,高于0。
3.
Thus the anodic polarization curves and pitting potentials of the BFe30-1-1 alloy in NaCl solutions of various pH values were measured.
5mol/LNaCl溶液中的阳极极化曲线以确定点蚀电位,并在点蚀电位之上进行恒电位腐蚀。
补充资料：硫化曲线
分子式：
CAS号：
性质：在某一温度下测定橡胶在硫化过程中某一物理性能与硫化时间关系的曲线。一般情况下，用硫化胶的拉伸强度、扯断伸长率、定伸应力和硬度等分别对硫化时间作图，就可以得到硫化曲线。目前通常用硫化仪直接绘出硫化曲线，由硫化曲线可以观察胶料硫化的整个过程，按橡胶交联情况的不同可分为:硫化诱导期、热硫化阶段、平坦硫化阶段和过硫阶段。从硫化曲线可以求得胶料焦烧性能、硫化速率、最佳硫化时间、硫化平坦性以及抗过硫返原性能等。
CAS号：
性质：在某一温度下测定橡胶在硫化过程中某一物理性能与硫化时间关系的曲线。一般情况下，用硫化胶的拉伸强度、扯断伸长率、定伸应力和硬度等分别对硫化时间作图，就可以得到硫化曲线。目前通常用硫化仪直接绘出硫化曲线，由硫化曲线可以观察胶料硫化的整个过程，按橡胶交联情况的不同可分为:硫化诱导期、热硫化阶段、平坦硫化阶段和过硫阶段。从硫化曲线可以求得胶料焦烧性能、硫化速率、最佳硫化时间、硫化平坦性以及抗过硫返原性能等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条