1) Ti 10V 2Fe 3Al Alloy
Ti10V-2Fe-3Al合金
2) Ti-10V-2Fe-3Al alloy
Ti-10V-2Fe-3Al合金
1.
The hot deformation behavior of two different microstructures of Ti-10V-2Fe-3Al alloy at temperature in the range of 650～900℃ and with strain rates from 0.
利用Gleeble3500热模拟试验机对Ti-10V-2Fe-3Al合金两种状态在不同变形温度及不同变形速率条件下的热变形行为进行了研究。
2.
Effect of β-fleck on properties of tensile elongation and low cycle fatigue life at room temperature for Ti-10V-2Fe-3Al alloy has been investigated.
研究了β斑点对Ti-10V-2Fe-3Al合金的室温拉伸性能和低周疲劳性能的影响,发现在β斑点区内,裂纹沿原始β晶界扩展形成沿晶脆性断裂,在交变应力作用下,β斑点往往成为疲劳源点,在高应变下,β斑区内的原始β晶界和晶界α处萌生裂纹并导致早期断裂。
3) Mg-3Al-1Zn alloy
Mg-3Al-1Zn合金
1.
In this paper the effects of Sr on the as-cast microstructure of Mg-3Al-1Zn alloy are investigated,and the results indicate that there are no obvious effects of adding 0.
结果表明:在Mg-3Al-1Zn合金中加入0。
2.
In this paper the effects of Y on the as-cast microstructure of Mg-3Al-1Zn alloy were investigated,and results indicated that the effects of 0.
结果表明,在Mg-3Al-1Zn合金中加入w(Y)=0。
3.
3%Y to Mg-3Al-1Zn alloy can refine the grains of the alloy, and adding Sr can obtain higher efficiency than adding Y.
Sr和Y以及不同Sr加入量对Mg-3Al-1Zn合金晶粒的细化效果差异与不同条件下Mg-3Al-1Zn合金的开始结晶温度不同有关。
4) AZ31(Mg-3AI-1.0Zn)magnesium alloy
AZ31(Mg-3Al-1.0Zn)镁合金
5) Ti-6Mo-25Nb-3Al alloy
Ti-6Mo-25Nb-3Al合金
6) Mg-11Li-3Al-0.5RE alloy
Mg-11Li-3Al-0.5RE合金
补充资料：Fe3Al基金属间化合物高温合金
Fe3Al基金属间化合物高温合金
Fe_(3)Al-base intermetallic compound superalloy
Fe3AI JIJ一nshujlon huahewu gaowen heJinFe3AI基金属间化合物高温合金(F e3AI一baseintermetallie eomPound suPeralloy)以Fe3AI相为基体的金属间化合物高温合金。该合金具有优异的高温抗氧化、抗硫化腐蚀性能，合金密度较小，因为不含贵重元素，故价格低廉，很适合于在高温氧化、硫化腐蚀的环境中工作。Fe3AI合金有两个不足之处:室温很脆，伸长率仅3%左右;高温强度不足。通过添加合金元素铬、硼，采取温加工工艺和合理的热处理制度，基本上解决了室温脆性问题，室温拉伸伸长率提高到15%左右。提高强度的途径是进行合金化，添加错、妮、铝等元素进行固溶强化和析出第二相进行时效强化，使合金室温拉伸强度达到l000MPa，600℃拉伸强度达到560MPa。Fe3AI基金属间化合物高温合金可以制造加热元件、炉子紧固件、热交换器、汽车用管材、石油管道和磁性元件等。该合金在真正走向实用之前，应在冶炼工艺和热加工工艺方面进行改进。 (}马培立卜
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条