1) BF return fines
高炉返矿
1.
The techniques of sinter charging to BF by size grading,and BF return fines screening were the first time employed in our country by ANGANG.
烧结矿分级入炉和高炉返矿筛分 ,是鞍钢二烧在国内首次采用的两项新技术。
2) blast furnace slag
高炉矿渣
1.
A large quantity of blast furnace slag discharged in Laiwu Steel Company causes serious environmental pollution.
莱钢每年排放大量的高炉矿渣造成了严重的环境污染,利用高炉矿渣生产微晶玻璃受到国内外的广泛关注。
2.
Replacement of pebbles with blast furnace slag for roadbed and road base cannot only solve the problem of transportation and construction cost,but can solve the problem of pollutions caused by abandoned blast furnace slag,which is significant for the alleviating material shortage,increasing the value of slag,comprehensive utilization and protection of the ecological environment.
高炉矿渣代替碎(卵)石作为公路路基、路面基层材料既可解决材料运距长、建设成本高的问题,又能解决被废弃高炉矿渣占用大量土地资源并对环境造成严重污染的问题,对缓解路用材料短缺,提高矿渣价值和综合利用率,以及保护生态环境等方面具有重大意义。
3.
In view of both the understanding of the double-interface sealing system and the basic analysis of the chemical and physical properties of blast furnace slag(BFS),a set of experimental facilities was developed for the simulation of interfacial bonding in cementing,and experimental evaluation was conducted on the performance of blast furnace slag cement system by bond strength simulation test.
基于对双界面封固系统的认识和对高炉矿渣物化特性的分析,研制了用于模拟固井界面胶结的试验装置,利用胶结强度模拟试验等方法评价了高炉矿渣水泥体系的性能。
3) slag
[英][slæɡ] [美][slæg]
高炉矿渣
1.
The flyash and slag, with standard sand as aggregate, were used as principal mat erials to prepare mineral polymer.
以粉煤灰,高炉矿渣为粉体原料,标准砂为骨料,采用振动成型方法,在蒸压釜中蒸压养护9h(养护温度为192℃),制备了矿物聚合材料。
2.
Glass-ceramic was made from the slag of Bao-Steel Corporation in Shanghai by body crystallization.
以宝钢高炉矿渣为原料整体析晶法制备矿渣微晶玻璃,通过DTA确定微晶玻璃的热处理制度,通过XRD确定玻璃的主晶相,利用SEM观察微晶玻璃的显微形貌,并对微晶玻璃的抗折强度进行测试。
4) Blast-furnace slag
高炉矿渣
1.
The method of preparing slag micro-crystallographic foamed glass by using blast-furnace slag,fly ash and waste glass as the main raw materials was discussed based on the composition range of micro-crystallographic foamed glass.
目的利用高炉矿渣、粉煤灰和废玻璃为原材料制备矿渣微晶泡沫玻璃,在确定微晶泡沫玻璃配方范围的基础上,对制备微晶泡沫玻璃的核化和晶化工艺参数进行了优化,使之具有轻质高强的优良性能。
2.
In the mixture with sulphur-rich tailings, the hydration reaction of blast-furnace slag has been studied by IR, XRD and SEM in order to understand the formation dynamics of ettringite.
用红外光谱、X射线衍射和扫描电子显微等现代微观微区测试手段 ,对高炉矿渣及含硫高的矿山尾矿砂混合体系的水化反应过程进行检测和分析 ,了解这一过程中新、旧物相的变化情况 ,通过对主要新生相钙矾石的生长和生成量的检测 ,选出理想的激发剂和合适的养护时间 ,从而给出以高炉矿渣作粘合剂 ,以富硫尾矿砂作骨料研制新型建筑材料的具体工艺条件。
3.
A comparison study has been made between the properties of blast-furnace slag powders (BFSP) ground in a φ750 mm×2 500 mm closed ball mill and in a vertical mill, respectively.
就小型立磨和闭路球磨 (75 0 m m× 2 5 0 0 m m) 2种粉磨系统制备的高炉矿渣粉体的基本特性进行了比较研究。
6) High Grade Blast Furnace
高炉富矿
补充资料：返矿率和返矿平衡
返矿率和返矿平衡
return fines and it's balance
生产率上升;但当返矿率达到一定值时，继续增加返矿 率则烧结生产率下降。所以对烧结矿生产来说，有一个 最佳返矿率，它可以使生产率达到最高点。(图1)他的fankuangIO he fankuang pingheng研究还表明:当料层高度(H)一定时，烧结矿的机械强返矿率和返矿平衡(return fines andlt，s度随着燃料比(占矿石量的百分数)及返矿率(占混合balance)铁矿石烧结后因强度较差和未完全烧要…叫水的高湿度的细精矿等返矿率一般较高，可达40%一返矿率/o/o50%。混合料的混合和制粒不好、烧结机的布料不均、图1烧结生产率与返矿率及燃料比的关系烧结点火热量不足、烧结终点控制不好或未能烧透以及烧结矿卸出后的多次破碎及筛分等都会增加返矿料量的百分数)的增加而增加，但当返矿平衡时，返矿率。此外，当烧结制度(如料层高度、点火温度、燃料用率增加，配入混合料的矿石及燃料量必然减少，因而烧量、抽风负压等)与原料性质不相适应，或烧结作业失结矿的机械强度也随之下降。(图2)导致烧结生产过常未能及时调整时，返矿率也会升高。返矿中如含有大程不稳定的另一原因，是进入烧结混合料中的热返矿量未经烧结的烧结混合料，则返矿细粉多、含碳高、质量的波动引起烧结混合料中水、碳的波动，因而导致烧量差，对烧结过程有不利的影响。质量良好的返矿多数结矿的产量及质量的波动。采用热冲击秤或将热返矿是已烧结成矿但机械强度较差的粒状物料，其粒度一经冷却后送入配料室参加配料，可以解决此项问题。般应在smm以下。返矿平衡烧结生产过程得以进行的必要条件。 返矿对烧结过程的影响质量良好的返矿可改善烧结机投产后，需要经过较长时间才能达到返矿平衡混合料的粒度组成，提高料层的透气性，特别是在细精(B二1)。如果返矿槽的料位增加，即B>l时，则可增矿烧结时，返矿有利于细精矿制粒，从而提高细精矿的加混合料中的燃料量以获得强度较大的烧结矿，促进烧结生产率。质量好的返矿在烧结过程中易形成液相平衡;如果返矿槽料位下降，使槽内存料有被用尽的危可增加烧结过程的液相量，从而提高了烧结矿的机械险时，要降低配加的燃料量，使返矿量增加。如果较长强度。对于脉石难熔的难烧矿粉，返矿的作用更加显时间内未能达到返矿平衡，表明烧结过程的目标参数著。德国卡佩尔(F、caPPel)的研究表明:在燃料配比与操作参数之间的关系不相适应，则应调整操作参数。(占矿石量)一定、烧结矿的机械处理流程一定、且保持同理，在烧结杯试验中也必须遵循这个原则加果没有返矿平衡的条件下，提高返矿率(占混合料量)，则烧结返矿平衡，很容易导致错误的结论。图3及图4示出返芝100厂，广一厂汽几汀茜二厂一下一下一犷门一 协90岁月，端乍脚碑共，卜叮号‘一斗，一书一+一州一川 姗一犷护了乳澎尹竺_。I卜义叼飞’.1’}}}】! 瑕n力.4岁尸，·。