1) Crack parting forging
断裂分开锻造
2) parting
[英]['pɑ:tɪŋ] [美]['pɑrtɪŋ]
分开的;断裂
3) forging crack
锻造裂纹
1.
A1N in Steel and its Affect on Forging Crack;
钢中的氮化铝及其对锻造裂纹的影响
2.
Through experiment found that the producing cause of forging cracks was oxide inclusions and composition segregation of Si、Mn element in original steel and non-suitable heating time for forging steel.
针对２０CrMnTiH钢锻造裂纹问题进行实验，发现锻造裂纹的产生原因是原始材中存在氧化物夹杂，硅、锰成分偏析以及锻造加热时间控制不当等。
4) forge crack
锻造裂纹
1.
This paper describes how the conclusion has been drawn from the metallurgical analysis that cracking in the bracket of hydraulic prop stand of 160t railway crane is not the quenching cracks caused by inapt quenching but rather micro forge cracks caused by non-metallic inclusion in forging blank before the bracket being heat-treated.
本文根据１６０吨铁路起重机支腿液压缸托架上裂纹的金相检验情况，分析得出裂纹产生的根本原因：裂纹并非热处理不当而引起的淬火裂纹，而是热处理以前就已存在于锻件毛坯中的，由钢中非金属夹杂物引起的微小锻造裂纹，因受热处理应力作用而扩展。
5) wet crack after forging
锻造湿裂
1.
By analyzing of the quality of material and heat treatment in detail through chemical and metallographic examination,the whole processing of causing crack and decarbonization was discussed and demonstrated and simulation test was made,the results proved that crack of bearing outer ring was wet crack after forging.
对某轴承套圈裂纹产生原因进行了分析,通过化学和金相检测,对套圈的材料质量和热处理质量进行全面分析,对裂纹和脱碳的产生进行整个工艺过程讨论和论证,并经摸拟试验,证明套圈裂纹是锻造湿裂。
6) forging internal crack
锻造内裂
补充资料：政企分开
| 政企分开 政府的职能与企业的职能分开。政企分开表明正确划分国家各级政权机构和经济组织的各自的权限，正确处理国家和企业的关系。 政府和企业是两类具有不同性质、任务、职能但又相互紧密联系的组织系统。政府是国家政权机构的具体形式，它的主要任务是治理国家，发挥国家机器的经济管理职能，通过一定的方式制约和影响整个社会的经济活动；企业是经济组织，它的主要任务是组织经济活动，并拥有必要的经营管理自主权，建立独立的生产系统和经营管理系统，将职工的经济利益同企业的经济成果挂钩，使责权利三者结合起来。因此，政府不宜于直接经营企业，企业要执行国家的法令、方针和政策，但不具备管理国家的职能。实行政企分开，可以减少政府对企业的控制和干预，扩大企业经营管理的自主权，使企业成为自主经营、自负盈亏、自我约束、自我发展的商品生产者和经营者。 |