1) Unit blank holder force
单位压边力
2) pressure
[英]['preʃə(r)] [美]['prɛʃɚ]
单位压力
1.
Calculating drum′s unit pressure by the iteration of layer by layer;
逐层迭代法计算卷取机卷筒单位压力
4) unit extrusion pressure
单位挤压力
1.
The paper researches on the relationship between C and Cr in steel product,deformation extent and unit extrusion pressure,taking experimental data of forward extrusion as the samples for training and predicting,predicts unit extrusion pressure using single hidden layer BP model with five nodes under Matlab language environment.
以钢材中C和Cr的成分、变形程度和单位挤压力的关系为研究对象,在Matlab语言环境下,以正挤压试验数据作为训练和预测样本,用5节点的单隐含层BP型神经网络对钢材单位挤压力进行了预测。
2.
The effect of billet size on the effective strain and unit extrusion pressure was investigated during equal channel angular pressing.
研究了坯料尺寸对等径角挤压材料等效应变及单位挤压力的影响。
5) p/σ(?)ratio
比单位压力
6) b (bar)
巴(压力单位)
补充资料：各种材料拉深时的单位压边力数据
在单动压力机上拉深时的单位压边力
材 料 | q/MPa |
铝 | 0.8～1.2 |
紫铜,杜拉铝(退火的或刚淬火的) | 1.2～1.8 |
黄铜 | 1.5～2.0 |
压轧青铜 | 2.0～2.5 |
20钢、08钢、镀锡钢板 | 2.5～3.0 |
软化耐热钢 | 2.8～3.5 |
高合金钢,高锰钢,不锈钢 | 3.0～4.5 |
在双动压力机上拉深时的单位压边力
工件复杂程度 | q/MPa |
难加工件 | 3.7 |
普通加工件 | 3.0 |
易加工件 | 2.5 |
材 料 | 单位压边力q/MPa |
铝(退火状态) | 0.8～1.2 |
铝(硬态) | 1.2～1.4 |
黄铜(退火状态) | 1.5～2.0 |
黄铜(硬态) | 2.4～2.6 |
铜(退火状态) | 1.2～1.8 |
铜(硬态) | 1.8～2.2 |
康铜BMn40-1.5(硬态) | 2.6～2.9 |
可伐合金4J29(退火状态) | 3.0～3.3 |
钼(退火状态) | 4.0～4.5 |
软钢t＜0.5mm | 2.5～3.0 |
软钢t＞0.5mm | 2.0～2.5 |
不锈钢1Cr18Ni9Ti | 4.5～5.5 |
镍铬合金Cr20Ni80 | 3.5～4.0 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。