1) SLS prototyping machine
SLS成形机
2) SLS rapid prototyping
SLS快速成形
1.
Closed-loop control and semi-closed-loop control for SLS rapid prototyping servo system are discussed and analyzed in this paper, and the dual-closed-loop control employed to achieve high accuracy for servo system is also presented.
讨论和分析了SLS快速成形伺服系统的闭环和半闭环控制,并提出了利用双闭环控制实现伺服系统的高精度控制。
2.
The control system and the key techniques of a new SLS rapid prototyping are studied systematically.
本文对新型SLS快速成形控制系统及关键工艺进行了深入的研究，在以下几个方面有一定的创新： 1。
4) SLS mechanism
SLS机理
6) selective laser sintering(SLS)
SLS
1.
For this reason,some new methods,technics and application examples of rapid manufacturing casting moulds based on the laminated object manufacturing(LOM)and selective laser sintering(SLS) series rapid prototyping (RP) system developed by Huazhong University of Science and Technology(HUST) are presented in this paper.
介绍了华中科技大学快速制造中心生产的薄材叠层(LaminatedObjectManufacturing LOM)和选择性激光烧结(SelectiveLaserSintering SLS)系列快速成形系统在铸造模具快速制造中的应用方法、工艺路线和实例。
2.
Curl distortion in the process of selective laser sintering(SLS) greatly affects the accuracy of the shaped parts by SLS.
选择性激光烧结工艺(selective laser sintering,SLS)加工中所产生的翘曲变形严重影响了成型件的加工精度和SLS技术的应用与推广。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。