1) Virtual Crack Extension Method
虚裂纹扩展法
1.
In this paper the virtual crack extension method is employed in the finite element analysis offracture problems.
本文将虚裂纹扩展法用于断裂问题的有限元分析，编制了计算二维Ⅰ型静态和动态Ｊ积分的程序，并对受静载的线弹性材料和线性硬化弹塑性材料的中。
2.
The paper investigates the delamination behavior caused by matrix cracking in laminated composite plates by 3D-finite element analysis and virtual crack extension method.
本文研究复合材料层板由于层内基体开裂所引起的分层问题,利用三维有限元和虚裂纹扩展法分析裂纹扩展的能量释放率,从而提供一个有效地预示裂纹形成和扩展规律的途径。
2) multiple virtual crack extension method
多虚拟裂纹扩展法
3) virtual propagation of microcracks
微裂纹虚拟扩展
4) Virtual crack extension
虚拟裂纹扩展
1.
Extended J-integration of different strength mismatched welded joint containing transverse crack under plain stress condition was calculated and modified using Delorenzi virtual crack extension method of MARC finite element program.
利用MARC有限元程序提供的Delorenzi虚拟裂纹扩展方法计算了平面应力条件下不同强度匹配的含横向裂纹的焊接接头模型在不同载荷下的广义J积分并对其进行了修正。
5) crack propagation
裂纹扩展
1.
Fatigue Fracture Morphology and Crack Propagation Mechanism of Die Cast AZ91 Alloy;
压铸态AZ91镁合金疲劳断口组织与裂纹扩展机制
2.
Mode Ⅰ crack tip plastic zone,dislocation-free zone and their effects on crack propagation;
Ⅰ型裂纹尖端塑性区和无位错区及其对裂纹扩展的影响
3.
On safety crack propagation life of welded structural members on offshore platforms;
海洋平台焊接构件的安全裂纹扩展寿命研究
6) crack expansion
裂纹扩展
1.
The purpose of Controlled Blasting Engineering is study the directed fracture of rock and the crack expansion.
工程控制爆破 ,要研究岩石的定向断裂的裂纹扩展。
补充资料：裂纹失稳扩展
分子式：
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。