1) hard agglomerate
硬团聚
1.
In preparation of ultratine Al 2O 2 powder by precipitation, ultrafine powder with a mean size of 0 47 μm and a specific surface area of 4 5560 m 2/g can be obtained by adding surfactant to control the size of particle and effectively elimination hard agglomerates by azeotropic distillation.
采用沉淀法制备超细氧化铝粉 ,通过添加表面活性剂控制颗粒的大小、共沸蒸馏处理有效地消除氢氧化铝凝胶的硬团聚 ,制得了平均粒度为d50 =0 47μm、比表面积BET =4 5 5 6 0m2 /g的超细粉
2.
Properties of nanometer ceramic powder, including high purity, controllable compositions, homogeneity, hoped phase, small particle size with sharp distribution, and no hard agglomerates are reviewed in detail.
着重介绍了纳米陶瓷粉末应具有的特性——高纯度、组成可控、成分均匀、具有所需物相、颗粒尺寸小且分布范围窄、无硬团聚体。
2) harden nano aggregation powder
纳米硬团聚体
3) agglomeration
[英][ə,ɡlɔmə'reɪʃn] [美][ə'glɑmə'reʃən]
团聚
1.
Preparation and agglomeration control of zirconia nano-powder by alcohol-aqueous co-precipitation method;
醇水共沉淀法制备氧化锆超细粉末及团聚控制
2.
Application of anti-static agents to eliminate ACF flock agglomeration;
抗静电剂在消除ACF绒团聚现象上的应用
3.
Agglomeration Problems and Anti-agglomeration Measures for the Preparation of Metal Oxide Nanoparticles;
纳米金属氧化物粉体制备过程的团聚问题和反团聚措施
4) aggregate
[英]['æɡriɡit] [美]['æɡrɪɡɪt]
团聚
1.
Parameter optimization of aggregate desulphurization process for high sulphur coal;
高硫煤团聚脱硫工艺参数优化
2.
Due to the great specific surface and surface energy, there are special domino effects that the powders are very easy to aggregate.
但因其具有极大的比表面积和表面能,因而极易团聚,致使其在应用中无法发挥纳米陶瓷的优异性能,但通过对纳米陶瓷表面改性可改善这一状况。
3.
Therefore hard aggregate was retarded in α phase transformation process.
利用NH4Cl其分解时释放气体的特点控制以碳酸铝铵为前驱体的氧化铝α相变过程中的团聚。
5) agglomerate
[英][ə'glɔmə,reɪt] [美][ə'ɡlɑmə,ret]
团聚
1.
The forming mechanism and the control of agglomerate are also concisely discussed.
ZrO2是结构陶瓷和功能陶瓷重要的原材料之一,有关纳米ZrO2粉体制备方法的研究有很多,本文介绍了近年来研究较多的液相制备纳米ZrO2粉体的方法,并对制备过程中粉体团聚的形成与控制做了简要论述。
2.
A technique of preparing nano Al 2O 3 powder by wet chemical method in supersonic field was studied, the effects of supersonic radiation on the formation and reunite of the grains were discussed, and the influence of different supersonic frequency on the agglomerate of the powder was researched.
研究了超声场下湿法制备纳米Al2 O3粉体的工艺 ,探讨了超声对颗粒的形成和团聚的影响 ,讨论了不同超声频率对粉体团聚的影响。
3.
The results showed that ultrasonic energy can speed up the nucleation of the precursor, ultrasonic dispersion can control the growth and agglomerate of the crystal nucleus, ultrasonic vibration can also affect the process of the transformation into gel during the process of aging, and was easy .
将超声波应用于湿法制备氧化铝纳米粉工艺过程 ,探讨了超声作用机理 ,研究了超声辐射对颗粒的形成和团聚以及干燥过程的影响 研究表明 ,超声能量能加速前驱体的形核 ,超声分散可控制晶核的长大和团聚 ;超声振动还能影响陈化过程中的沉淀向凝胶的转变 ,易得到疏松三维网络状结构 ,这样的凝胶结构有利于最后得到疏松、少 (无 )团聚的纳米粉
6) agglomerate
[英][ə'glɔmə,reɪt] [美][ə'ɡlɑmə,ret]
聚团
1.
The experimental results indicate that the large agglomerates of SiO_2 nano -particles can be broken up through the vibration of the coarse magnets under AC oscillating magnetic field.
研究了纳米SiO_2在添加磁性大颗粒磁场流化床中的流化性能,实验中通过测量其床层膨胀曲线、床层压降曲线以及塌落曲线表明:磁性大颗粒在交变磁场下的振动作用可以破碎流化床中纳米SiO_2的大聚团,使床层压降和床层膨胀明显增大,流化质量获得显著提高。
2.
The effects of sound wave on the fluidization behaviors and agglomerate size were discussed.
在内径为56 mm的声场流化床中,以超细颗粒二氧化硅为实验物料,在声压水平为90~105 dB系统内考察了声波对超细颗粒流化行为和聚团尺寸的影响,并根据粘性颗粒聚团在流化床中的能量平衡分析,建立了能量平衡模型。
3.
With increasing the superficial gas velocity, slugs and channels vanished, whilst the bubbling in bed was intensified obviously, and there existed a distribution of agglomerate sizes, namely, the agglomerates sizes were small in the upper zone and lar.
振动有效地减小了聚团尺寸,提高了床层的气含率,明显改善了流化效果。
补充资料：超硬刀具及其在硬车削加工中的应用
随着现代科学技术的发展，各种高硬度的工程材料越来越多地被采用，而传统的车削技术难以胜任或根本无法实现对某些高硬度材料的加工。涂层硬质合金、陶瓷、PCBN等超硬刀具材料因其具有很高的高温硬度、耐磨性和热化学稳定性，这为高硬度材料的切削加工提供了最基本的前提条件，并在生产中取得了明显效益。 超硬刀具及其选用 超硬刀具采用的材料及其刀具结构和几何参数是实现硬车削的基本要素，因此，如何选择超硬刀具材料，设计出合理的刀具结构和几何参数对稳定实现硬车削是十分重要的。 1，超硬刀具材料及其选用 涂层硬质合金 在韧性较好的硬质合金刀具上涂覆1层或多层耐磨性好的TiN、TiCN、TiAlN和Al3O2等，涂层的厚度为2~18µm，涂层通常具有比刀具基体和工件材料低得多的热传导系数，减弱了刀具基体的热作用；另一方面能有效地改善切削过程的摩擦和粘附作用，降低切削热的生成。 涂层按生成方法可分为物理气相沉积(PVD)与化学气相沉积(CVD)2种。PVD涂层(2~6µm)主要包括TiN、TiCN、TiAlN等，其成分还在不断地增加，如TiZrN。TiN和TiC涂层的最高压力分别可达到3580MPa和3775MPa，TiAlN涂层因缺乏可靠的弹性模量数据而得不到准确的压应力值，高速切削实验结果表明TiAlN性能最好。图1为这3种涂层硬度随温度变化的情况，在室温下硬度最高，当温度超过[Y;\时，TiAlN涂层的硬度高于TiCN和TiN涂层。图2为加工镍基高温合金Inconel178时用2种切削速度v1=193.5m/min和v2=380m/min条件下的刀具寿命，实验表明TiCN和TiAlN涂层的切削性能明显优于TiN涂层。 
尽管PVD涂层显示出很多优点，但一些涂层如Al2O3和金刚石则倾向于采用CVD涂层技术。Al2O3是一种耐热和抗氧化很强的涂层，它能够将刀具体和切削产生的热量隔离开。通过CVD涂层技术，还可以综合各种涂层的优点，以达到最佳的切削效果，满足切削加工的需要。例如。TiN具有低摩擦特性，可减少涂层组织的损耗，TiCN可降低后刀面的磨损，TiC涂层硬度较高，Al2O3涂层具有优良的隔热效果等。
涂层硬质合金刀具与硬质合金刀具相比，无论在强度、硬度和耐磨性方面均有了很大提高。车削硬度在HRC45~55的工件，低成本的涂层硬质合金可实现高速车削。近年来，一些厂家应用改进涂层材料等方法，使涂层刀具的性能有了极大的提高。如美、日的一些厂家采用瑞士AlTiN涂层材料和新涂层专利技术生产的涂层刀片，硬度高达HV4500~4900，可在498.56m/min的速度时切削硬度HRC47~58的模具钢。在车削温度高达1500~1600°C时仍然硬度不降低、不氧化，刀片寿命为一般涂层刀片的4倍，而成本只有30%，且附着力好。