1) LF21 Al alloy
LF21防锈铝
2) LF21 aluminum alloy
LF21铝合金
1.
Study on microstructure and properties of LF21 aluminum alloy after equal channel angular pressing;
LF21铝合金等通道转角挤压后的组织性能研究
2.
Microstructure in friction stir welding of thick LF21 aluminum alloy
LF21铝合金厚板搅拌摩擦焊接接头微观组织研究
3.
It shows that the welding adaptability of LF21 aluminum alloy is good.
4 mm的LF21铝合金薄板进行单道对接焊实验。
3) aluminum alloy LF21
铝合金LF21
1.
Electron Beam welding was carried out to study the mechanism of activating flux improving weld penetration for aluminum alloy LF21.
为了研究铝合金焊缝熔深增加机理,利用电子束散焦焊的焊接方法对铝合金LF21进行了焊接。
4) corrosion-resisting aluminum alloy
防锈铝
1.
Upon wide application of corrosion-resisting aluminum alloy and carbon fiber composite to aerospace industry,the contact between them is inevitable.
随着防锈铝和碳纤维复合材料在航空航天工业的广泛应用,它们间的接触不可避免。
5) alumite LF6
防锈铝LF6
1.
Integrating with the finite element method, the hydro-mechanical deep drawing of alumite LF6 was simulated.
根据模具几何特征 ,通过建立流体力学模型描述液体对板料单元的动态影响 ,结合有限元数值模拟技术对塑性差、难成形材料防锈铝LF6的充液拉深进行数值模拟 ,并进行实验研究 ,得到了防锈铝充液拉深合理工艺参数。
6) Anti-rust aluminum plate
防锈铝板
补充资料：防锈铝合金
分子式：
CAS号：
性质：在大气、水和油等介质中具有良好抗腐蚀性能的可压力加工铝合金。主要包括不能热处理强化的Al-Mn系和Al-Mg系合金。含锰量在1.0%～1.7%的防锈铝合金，抗腐蚀性能较高。而Al-Mg系防锈铝合金中镁含量一般不超过7%，随着含镁量的增加，合金的强度增大，σ0可达400MPa，而塑性则下降。这一类防锈铝合金通常在退火状态、冷作硬化或半冷作硬化状态下使用。强度低、塑性好、易于压力加工，具有良好的抗腐蚀性能和焊接性能特别适宜于制造承受低载荷的深拉伸零件、焊接件和在腐蚀介质中工作的零件，如油箱、管道等。另一类防锈铝合金是可热处理强化的Al-Zn-Mg-Cu系合金，其拉伸强度较高，具有优良的耐海水腐蚀性能，良好时断裂韧性，低的缺口敏感性和好的成型工艺性能。适于制造水上飞机蒙皮及其他要求耐腐蚀的高强度钣金零件。
CAS号：
性质：在大气、水和油等介质中具有良好抗腐蚀性能的可压力加工铝合金。主要包括不能热处理强化的Al-Mn系和Al-Mg系合金。含锰量在1.0%～1.7%的防锈铝合金，抗腐蚀性能较高。而Al-Mg系防锈铝合金中镁含量一般不超过7%，随着含镁量的增加，合金的强度增大，σ0可达400MPa，而塑性则下降。这一类防锈铝合金通常在退火状态、冷作硬化或半冷作硬化状态下使用。强度低、塑性好、易于压力加工，具有良好的抗腐蚀性能和焊接性能特别适宜于制造承受低载荷的深拉伸零件、焊接件和在腐蚀介质中工作的零件，如油箱、管道等。另一类防锈铝合金是可热处理强化的Al-Zn-Mg-Cu系合金，其拉伸强度较高，具有优良的耐海水腐蚀性能，良好时断裂韧性，低的缺口敏感性和好的成型工艺性能。适于制造水上飞机蒙皮及其他要求耐腐蚀的高强度钣金零件。