1) initial crystallization temperature
等溶初晶温度
1.
According to the regression equations of initial crystallization temperature(ICT), the solubility of alumina and density at the temperature of 20 ℃ above its ICT of (2.
0 )NaF·AlF3 ( 0～ 5% )LiF ( 0～ 1 5% )CaF2 系熔体初晶温度、变温氧化铝溶解能力和变温密度的研究 ,首次得到了氧化铝溶解能力为 6% ,8%和 1 0 %时温度范围在 91 0～ 950℃的等溶初晶温度和密度在2 。
2) liquidus temperature
初晶温度
1.
Effect of NaCl and LiF on liquidus temperature of molten cryolite-based aluminum electrolyte;
NaCl和LiF的添加对铝电解质初晶温度影响的研究
2.
Study on new device for testing liquidus temperature of aluminium electrolyte and mathematical model of liquidus temperature;
铝电解质初晶温度测定装置及初晶点数模的研究
3.
Study on direct determination of liquidus temperature of aluminium electrolyte;
直接测定铝电解质初晶温度的研究
3) isothermal solubility
等温溶解度
4) solubility isotherm
溶度等温线
5) primary silicon growth temperature
初晶生长温度
1.
08%), the average grain size of the primary silicon decreases, the primary silicon growth temperature TG and its difference ΔTG increase; the different holding time has little effect on the average grain size of the primary silicon and ΔTG.
08%),初晶Si平均晶粒尺寸减小,初晶生长温度TG及其差值ΔTG不断增大;在变质处理后不同的保温时间下平均晶粒尺寸及ΔTG都变化不大。
6) density at nonequal temperature
等溶变温密度
1.
Initial crystallization temperature and density at nonequal temperature of Na_3AlF_6-AlF_3-LiF-CaF_2 system under isosolubity of alumina;
Na_3AlF_6-AlF_3-LiF-CaF_2系熔体的等溶初晶温度和等溶变温密度
补充资料：会溶温度
分子式：
CAS号：
性质：也称临界溶解温度(critical solution temperature)。两个部分互溶的液体(例如水和苯胺)形成的系统，在一定温度达到平衡时，有两个液相共同存在。其中一个液相是苯胺在水中的饱和溶液，另一液相则是水在苯胺中的饱和溶液。两个饱和溶液有时称为共轭溶液(conjugate solution)，它们不能再互溶。升高温度(对有些共轭溶液是降低温度)，两共轭溶液的互溶度增加，直到某一个温度，两共轭溶液开始完全互溶而成为一相。这一温度称为会溶温度。在会溶温度以上(或以下)只有一个液相存在。
CAS号：
性质：也称临界溶解温度(critical solution temperature)。两个部分互溶的液体(例如水和苯胺)形成的系统，在一定温度达到平衡时，有两个液相共同存在。其中一个液相是苯胺在水中的饱和溶液，另一液相则是水在苯胺中的饱和溶液。两个饱和溶液有时称为共轭溶液(conjugate solution)，它们不能再互溶。升高温度(对有些共轭溶液是降低温度)，两共轭溶液的互溶度增加，直到某一个温度，两共轭溶液开始完全互溶而成为一相。这一温度称为会溶温度。在会溶温度以上(或以下)只有一个液相存在。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条