1)  non isothermal curing
变温硫化
2)  RTV
室温硫化
1.
Study of Mechanical Properties of RTV Silicone Sealant Modified by Carbonyl Iron Powder;
羰基铁粉填充室温硫化有机硅密封胶力学性能的研究
2.
Study on one-component condensating type RTV fluorosilicone adhesive;
单组分缩合型室温硫化氟硅橡胶胶粘剂的研制
3.
Study on water-based RTV silicone rubber having self-catalytic crosslinker;
自催化交联体系室温硫化水性硅橡胶研究
3)  curing temperature
硫化温度
1.
The curing temperature of9 00-2016PR tire in autoclave was determined withJLW 12 Curing Temperature Tester.
00-2016PR轮胎进行硫化温度测定,获得了硫化温度在轮胎各部位的变化情况,并以此得到各部位胶料的硫化程度,发现均存在过硫现象,适当调整工艺条件,硫化外温由143℃改为151℃,硫化时间缩短5min后,轮胎机床耐久性能提高显著。
2.
Study on property and curing temperature of low elasticity shock-absorbing blowing material;
较好的硫化温度为433~443K,最佳温度为438K。
4)  room temperature vulcanization
室温硫化
1.
The development of room temperature vulcanization silicone rubber and water based silicone rubber was reviewed The preparation method and crosslinking mechanism of water based silicone rubber were introduced The crosslinking mechanism,capability and applications of water based silicone rubber were described in detail
简要回顾了室温硫化硅橡胶及水基硅橡胶的发展过程 ,介绍了水基硅橡胶的制备方法及交联机理 ,并对其交联过程、性能及用途作了较详细的阐述。
2.
Addition-cured room temperature vulcanization silicone rubber can be vulcanized in room temperature with no small molecules be emitted and no heat and shrinkage be generated during vulcanization.
加成型室温硫化硅橡胶因其硫化反应是在室温下进行,在硫化交联过程中不放出低分子物,不发热、不收缩;硫化后的硅橡胶无毒、机械强度高、具有卓越的抗水解稳定性、良好的低压缩形变、低燃烧性、可深度硫化、以及硫化速度可以用温度来控制等优点,因此自问世以来立即受到各工业部门的关注,并进行了大量的应用工作。
3.
Addition-cured room temperature vulcanization silicone rubber has the advantages of favorable handling properties, short setting time, producing no outgrowth, and dimensional stability, which have resulted in its popularity in many industrial fields.
加成型室温硫化硅橡胶因具有制造简单、使用方便、固化交联反应不产生副产物、可深层硫化、操作时间可控制、介电性能优良、线收缩率低等优点已在各个工业部门得到了广泛应用。
5)  room temperature vulcanized
室温硫化
1.
One-part room temperature vulcanized fluorosilicone rubber(FR1)containing ND-42(phenylaminomethyl triethoxysilane)as crosslinker and dibutyltin dilaurate as condensation catalyst can cure quickly and has good adhesive properties.
研究以苯胺甲基三乙氧基硅烷(南大-42)为交联剂的单组分缩合型室温硫化氟硅橡胶和以硅氮化合物KH-CL或正硅酸乙酯为交联剂的双组分缩合型室温硫化氟硅橡胶的硫化性能及其粘接性能。
6)  initial vulcanization temperature
硫化初温