1) deacetonized RTV 1 silicone rubber
脱丙酮型RTV-1硅橡胶
2) dealcoholized RTV-1 silicone rubber
脱醇型RTV-1硅橡胶
1.
The effects of calcium chloride anhydrous content on properties of dealcoholized RTV-1 silicone rubber before and after an accelerating storage were studied.
研究了氯化钙用量对脱醇型RTV-1硅橡胶模拟加速储存前后的性能影响,结果表明:氯化钙缩短了硅橡胶的表干时间,改善了硅橡胶的储存性能,但随着氯化钙用量增加,硅橡胶力学性能均逐渐下降;氯化钙用量为10份时,硅橡胶各方面性能在加速储存前后均保持较佳,但是热稳定性下降严重。
2.
Dealcoholized one component room temperature vulcanizing(RTV-1)silicone rubber was prepared withα,ω-dihydroxy dimethylsiloxane as matrix with additives and effects of contents of reinforcing agent(white carbon black,calcium carbonate),cross linking agent and catalyst on performance of dealcoholized RTV-1 silicone rubber were studied.
用α,ω-二羟基聚二甲基硅氧烷为基料,配合其他助剂,制备出脱醇型单组分室温硫化(RTV-1)硅橡胶,并研究了补强剂(白炭黑、碳酸钙)、交联剂和催化剂用量对脱醇型RTV-1硅橡胶性能的影响。
3) RTV-1 silicone
RTV-1硅橡胶
1.
Particularly the effects of amount of active nano-fillers, molecular weight of hydroxyl-terminated polydimethylsiloxane, and amount crossing agent and coupling agent on the performance of RTV-1 silicone were investigated.
并研究了该体系对脱酮肟密封胶性能的影响及活性纳米填料用量、端羟基聚二甲基硅氧烷(107胶)分子质量、交联剂和偶联剂用量等对RTV-1硅橡胶性能的影响。
4) deacetonized RTV silicone rubber
脱丙酮型室温硅橡胶
5) RTV silicone rubber
RTV硅橡胶
1.
Study on surface treatment of calcium carbonate and its uses in RTV silicone rubber(Ⅱ);
超细碳酸钙表面处理及其在RTV硅橡胶中的应用(二)
2.
Study on increasing the strength of bonding for RTV silicone rubber by bis(β-azidoformyloxy-ethyl) isophthalate;
间苯二甲酸二(β叠氮甲酰氧基乙酯)提高RTV硅橡胶粘接强度研究
3.
The effect of coupling agent b on the adhesion strength of RTV silicone rubber;
偶联剂B对RTV硅橡胶粘接强度的影响
6) hexa-functional ethylidyne siloxane
RTV导电硅橡胶
1.
A new hexa-functional ethylidyne siloxane was synthesized through hydrosilicone addition reaction, and the siloxane was characterized by FT-IR spectra and GC-MS spectra.
以此六官能度乙撑硅氧烷作为交联剂,与107胶、填料、乙炔炭黑,催化剂配混,制备双组分脱醇型RTV导电硅橡胶。
补充资料：methyl block RTV silicone rubber adhesive
分子式：
CAS号：
性质：硫化前为流动的黏稠液到不流动的膏状物。硫化胶的拉伸强度4~6MPa，相对伸长率200%～500%，使用温度范围-60～200℃。由羟基封端的二甲基聚硅氧烷和甲基三乙氧基硅烷的低聚体以7：3或5：5的比例混合配制成胶料，配制时也可加入适量的气相法白炭黑。使用前，加入0.5%～2%的二丁基二月桂酸锡催化剂。硫化过程中发生嵌段共聚反应，提高了硅橡胶的强度。用作黏合剂、灌注料、密封、浸渍、印模及脱模材料。
CAS号：
性质：硫化前为流动的黏稠液到不流动的膏状物。硫化胶的拉伸强度4~6MPa，相对伸长率200%～500%，使用温度范围-60～200℃。由羟基封端的二甲基聚硅氧烷和甲基三乙氧基硅烷的低聚体以7：3或5：5的比例混合配制成胶料，配制时也可加入适量的气相法白炭黑。使用前，加入0.5%～2%的二丁基二月桂酸锡催化剂。硫化过程中发生嵌段共聚反应，提高了硅橡胶的强度。用作黏合剂、灌注料、密封、浸渍、印模及脱模材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。