1) X zeolite
X沸石
1.
The large single crystals of X zeolite containing functional complex have been synthesized using a direct crystallization method and characterized by means of X ray diffraction spectroscopy, UV visible spectroscopy, emission spectroscopy and element analysis.
采用直接晶化方法合成含功能配合物的 X沸石大单晶 ,应用 X射线衍射、紫外 -可见光谱、发光光谱和元素分析等多种方法对产物进行表征 。
2) zeolite X
沸石X
1.
Equilibrium studies for C4 hydrocarbonsadsorption onto cation exchanged zeolite X;
阳离子交换的沸石X对丁烷/丁烯吸附平衡的研究(英文)
3) zeolite X
X型沸石
1.
On the basis of many experiments,the influence of the aging time of the reactant in room temperature and hydrothermal reaction time of reaction mixture on the preparation of zeolite X were particularly studied.
分析了反应混合物的室温陈化时间以及水热反应时间对酸处理红辉沸石制备X型沸石的影响。
2.
Taking acid-treated stellerite as main material, zeolite X powder was prepared by hydrothermal method.
以酸处理红辉沸石为主要原料 ,采用水热法制备了X型沸石粉体。
4) Na-X zeolite
Na-X沸石
1.
Na-X zeolites were successfully synthesized using the coal fly ash from a thermo-electric plant in Taiyuan by fusion method.
以太原某热电厂粉煤灰为原料,采用碱熔融法,考察了碱度、晶化温度和晶化时间对合成Na-X沸石的影响。
5) low silica X zeolite
低硅X沸石
6) Low-silica X-zeolite(LSX)
低硅X型沸石(LSX)
补充资料：4A沸石
分子式：
CAS号：
性质：又称Na12[(A1O2)12、(SiO2)12]27H2O 又称4A分子筛。白色固体颗粒。呈网络状结构，内含均匀小孔，孔径0.42nm，比表面积约为600m2/R，不溶于水和有机溶剂，能溶解于强碱和强酸。加热超过800℃时，重新结晶形成白硅石状的结构。有吸附水分，液体、气体及不饱和的有机物质。对钙离子有交换能力，理论交换能力为352CaCO3mg/g，一般为290～320mgCaCO3/g，白度≥95%，pH值10～11.5，表观密度0.3～0.5g/cm3，平均粒径为2μm，粒度分布≤4μm占85%以上。用作无磷洗涤剂的助剂，代替三聚磷酸钠；在石油和其他工业用作气体和液体的干燥、脱水净化等，也用作催化剂和软水剂。
CAS号：
性质：又称Na12[(A1O2)12、(SiO2)12]27H2O 又称4A分子筛。白色固体颗粒。呈网络状结构，内含均匀小孔，孔径0.42nm，比表面积约为600m2/R，不溶于水和有机溶剂，能溶解于强碱和强酸。加热超过800℃时，重新结晶形成白硅石状的结构。有吸附水分，液体、气体及不饱和的有机物质。对钙离子有交换能力，理论交换能力为352CaCO3mg/g，一般为290～320mgCaCO3/g，白度≥95%，pH值10～11.5，表观密度0.3～0.5g/cm3，平均粒径为2μm，粒度分布≤4μm占85%以上。用作无磷洗涤剂的助剂，代替三聚磷酸钠；在石油和其他工业用作气体和液体的干燥、脱水净化等，也用作催化剂和软水剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条