1) spherical zirconia particles
球形氧化锆粉体
3) spherical zirconia
球形氧化锆
1.
Preparation of spherical zirconia by the wet chemical method;
球形氧化锆的湿法制备过程研究
2.
Preparation of spherical zirconia and Ni-coated zirconia composite powders;
球形氧化锆及氧化锆/镍复合粉体的制备
4) ZrO_2 powder
氧化锆粉体
1.
The dried gel was calcined to ZrO_2 powder.
以氧氯化锆为前驱体,采用溶胶-凝胶法快速制备锆溶胶,凝胶后经煅烧制得氧化锆粉体,分析了锆溶胶的制备、稳定和氧化锆粉体的特性。
5) zirconia powder
氧化锆粉体
1.
In this paper, Zr(OR) 4 synthesised in lab is selected as a precursor to prepare zirconia powder by sol gel process.
选用实验室合成的醇盐锆为前驱体，采用ｓｏｌｇｅｌ工艺制备了氧化锆粉体。
6) hollow sphere-shaped zirconium oxide
空心球形氧化锆
1.
Through the research on the application of hollow sphere-shaped zirconium oxide powder in aero-engine field, hollow sphere-shaped zirconium oxide powder turns out to has higher deposit efficiency, less coating void, better powder liquidity and high-temperature thermal-resistant effect, besides stronger oxidation-resistant ability of bonder course compared with multi-edged zirconium oxide powder.
通过对空心球形氧化锆粉末在航空发动机上的应用研究,对比试验得出了空心球形氧化锆粉末比多棱体氧化锆粉末具有沉积效率高、涂层孔隙少、粉末流动性好、高温隔热效果好和防止结合层氧化能力强等优点。
补充资料：氧化锆-氧化钇红外陶瓷
分子式： ZrO2-Y2O3
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。