1) poly(paraphenylene)(PPP)
聚对苯薄膜
1.
Ion beam effects on poly(paraphenylene)(PPP) film under the ion implantation with potassium ions(K +) and argon ions(Ar +) have been investigated through the FT IR and the temperature dependence of the surface resistivity.
当 2 0～ 70 ke V的 Ar+和 N+注入后 ,聚对苯薄膜的电导率随着剂量的增加而迅速增加。
2) parylene film
聚对二甲苯薄膜
1.
The structure and properties of parylene films were characterized and measured by AFM,FTIR,XPS,UV-VIS-NIR,etc.
采用原子力显微镜、红外光谱、X射线光电子能谱、紫外-可见-近红外分光光度计的测试方法,对聚对二甲苯薄膜的表面形貌、组成和光学性能进行研究。
3) poly (p phenylene vinylene) thin film
聚对苯乙炔薄膜
4) Parylene C Film
聚氯代对二甲苯薄膜
1.
Study of Thermal Aging Property of Parylene C Film;
聚氯代对二甲苯薄膜热氧老化性能研究
5) parylene films
聚对二甲苯类薄膜
1.
Encapsulation of organic light-emitting devices by parylene films
聚对二甲苯类薄膜用于有机电致发光器件的封装
6) polyaniline film
聚苯胺薄膜
1.
Growth of polyaniline film in different protonic acids
聚苯胺薄膜在不同质子酸溶液中的生长
2.
Ion beam effects on polyaniline film are studied for ion implantation with nitrogen ions (N +).
研究发现,本征态聚苯胺薄膜的电导率随着注入能量的增加而迅速增加,但随注入剂量的增加程度较缓慢,当能量增至36keV时,电导率增加9个数量级。
补充资料：聚对苯二甲酰对苯二胺纤维
分子式：
CAS号：
性质： 由对苯二甲酸或二酰氯与对苯二胺缩聚纺成的纤维，中国称芳纶Ⅱ。密度1.44～1.47g/cm3，强度15～26cN/dtex，伸长率1.2％～6.0％，模量450～1130cN/dtex，极限氧指数26，玻璃化温度240℃、分解温度550℃，抗冲击强度和冲击吸收能高，耐磨性好。制法是将上述两单体进行低温溶液缩聚，再将高分子树脂溶于浓硫酸中干喷湿纺，必要时高温热处理以提高模量。用作轮胎等橡胶补强材料、复合材料增强剂、光缆增强芯、防弹背心、体育用品、摩擦和制动材料、缆绳类、头盔、火箭发动机壳体、坦克复合装甲、防切割和防火服、工业帆布、新型代钢筋建材和混凝土结构物修补加固材料等。
CAS号：
性质： 由对苯二甲酸或二酰氯与对苯二胺缩聚纺成的纤维，中国称芳纶Ⅱ。密度1.44～1.47g/cm3，强度15～26cN/dtex，伸长率1.2％～6.0％，模量450～1130cN/dtex，极限氧指数26，玻璃化温度240℃、分解温度550℃，抗冲击强度和冲击吸收能高，耐磨性好。制法是将上述两单体进行低温溶液缩聚，再将高分子树脂溶于浓硫酸中干喷湿纺，必要时高温热处理以提高模量。用作轮胎等橡胶补强材料、复合材料增强剂、光缆增强芯、防弹背心、体育用品、摩擦和制动材料、缆绳类、头盔、火箭发动机壳体、坦克复合装甲、防切割和防火服、工业帆布、新型代钢筋建材和混凝土结构物修补加固材料等。