1) poly(ethyl acrylate) emulsion
聚丙烯酸乙酯乳液
2) polyacrylate emulsion
聚丙烯酸酯乳液
1.
Application of ANN in property prediction of polyacrylate emulsion;
ANN在聚丙烯酸酯乳液性质预测中的应用
2.
Factors of Affecting Polyacrylate Emulsion Adhesive Properties;
影响聚丙烯酸酯乳液胶粘剂性能的因素
3.
Study on synthesis of polyacrylate emulsion modified by silica sol via in-situ polymerization
硅溶胶原位改性聚丙烯酸酯乳液的研究
3) polyacrylate latex
聚丙烯酸酯乳液
1.
The organosiloxane modified core-shell polyacrylate latex(ACR Latex) was prepared from acrylate monomer and A-174, by emulsion polymerization.
以丙烯酸酯类单体及γ-甲基丙烯酰氧基丙基三甲氧基硅烷(A-174)等为原料,乳液聚合制备了有机硅改性的核-壳型聚丙烯酸酯乳液(简称ACR乳液),考察了ACR乳液质量分数、交联剂质量分数、固化温度及固化时间等因素对其固砂效果的影响。
2.
The ambient self-crosslinkable polyacrylate latexes with sealed function were synthesized by semi-batch seeded emulsion polymerization with diacetone acrylamide(DAAM),methyl acrylate(MMA),methacrylic acid(MAA) and butyl acrylate(BA) as co-monomers.
以双丙酮丙烯酰胺(DAAM)、甲基丙烯酸甲酯(MMA)、丙烯酸丁酯(BA)和甲基丙烯酸(MAA)为共聚单体,采用半连续种子乳液聚合工艺合成自交联封闭性聚丙烯酸酯乳液(PAE),考察了DAAM和复合乳化剂对乳液聚合稳定性以及涂膜性能的影响。
4) acrylic emulsion
聚丙烯酸酯乳液
1.
Ni electrode-multilayer ceramic capacitor(Ni-MLCC) was prepared by aqueous tape-casting of X7R with acrylic emulsion as binders.
以聚丙烯酸酯乳液为粘合剂,采用水基流延成型制备镍电极多层陶瓷电容器(Ni-MLCC)。
5) vinyl acetate/acrylate emulsion
醋酸乙烯酯-丙烯酸酯共聚乳液
6) copolymer emulsion of VAc-Veova 10-acrylic ester
醋酸乙烯酯-叔碳酸乙烯酯(veova10)-丙烯酸酯共聚乳液
补充资料：聚丙烯酸乙酯
分子式：
CAS号：
性质： 丙烯酸乙酯的均聚物和共聚物。本体自聚物是柔软富延展性的无色透明橡胶态物质。玻璃化温度-24℃。伸长率1800％。密度为1.12g/cm3。折射率1.464。拉伸强度0.23MPa。溶解性类似于聚丙烯酸甲酯。主要用作丙烯酸酯橡胶的基材。乳液聚合物与溶液聚合物一般为共聚物，丙烯酸乙酯是“软单体”组分，成膜软硬度适中，适用于作织物和皮革处理剂。
CAS号：
性质： 丙烯酸乙酯的均聚物和共聚物。本体自聚物是柔软富延展性的无色透明橡胶态物质。玻璃化温度-24℃。伸长率1800％。密度为1.12g/cm3。折射率1.464。拉伸强度0.23MPa。溶解性类似于聚丙烯酸甲酯。主要用作丙烯酸酯橡胶的基材。乳液聚合物与溶液聚合物一般为共聚物，丙烯酸乙酯是“软单体”组分，成膜软硬度适中，适用于作织物和皮革处理剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。