1) unrecrystallized austenite deformation
奥氏体未结晶区变形
2) austenite non-recrystallization region
奥氏体未再结晶区
1.
The effect of thermomechanical treatment processing(immediate quenching after deformation in the austenite non-recrystallization region)on microstructures of T91 ferritic heat resistant steel was investigated by compressive deformation performed on a Gleeble 1500 thermomechanical simulator.
在 Gleeble 1500热模拟实验机上采用热压缩实验方法,研究了形变热处理工艺即在奥氏体未再结晶区变形后直接淬火对 T91铁素体耐热钢微观组织的影响。
3) undeformed austenite
未变形奥氏体
1.
The observations by OM and TEM reveal that when undeformed austenite continuously cooled at 10 to 30℃/s,bainitic ferrite nucleated mainly at austenite grain boundaries,grown up like parallel lath into the bulk from the grain boundaries of austenite,and original austenite grain boundaries could be seen.
经OM和TEM观察表明,当未变形奥氏体以10~30℃/s连续冷却时,贝氏体铁素体优先在奥氏体晶界处形核,然后呈板条状从奥氏体晶界向晶内长大,并且可以从最终的组织看到原奥氏体晶界。
4) unchanged austenite
未变奥氏体
5) Ausrenitic complete recrystallization region
奥氏体完全再结晶区
6) Recrystallization of Austeniting phase transition
奥氏体相变再结晶
补充资料：奥氏体-贝氏体球铁
分子式：
CAS号：
性质：又叫奥-贝球铁。基体组织为奥氏体加贝氏体组织的球墨铸铁。这类球铁硅含量一般在1.4%～3.8%。含锰量小于0.5%，与普通球铁比较硅偏高、锰偏低。通过调节化学成分与热处理获得理想的奥-贝球铁的基体组织为针状贝氏体或无碳贝氏体一富碳奥氏体。这类球铁具有优良的综合机械性能、强度高、耐磨性好、韧性好、特别是有高的缺口韧性，可代替钢，用于制作重要受力结构件，如曲轴、齿轮、凸轮轴等。