1) lining plate
分料盘
1.
The wear mechanism of the lining plate of concrete spurt machine has been studied by testing wear rate and toughness for samples treated in various heat treatments and by observing the worn surface using scanning electron microscope (SEM).
从锚喷机分料盘（俗称衬板）的实际工作情况出发，着重对不同热处理工艺下的试样进行磨损和冲击试验，并借助扫描电镜观察，研究了高铬白口铸铁分料盘的磨损机理；分析其影响磨损的主要因素，最终找出一个硬度和韧性最佳匹配的工艺来提高分料盘使用寿命。
2.
According to the actually operation condition of the lining plate of concrete shotting machine, the wear mechanism of the lining plate has been analyzed with SEM.
从矿用锚喷机分料盘的实际工作条件出发，利用扫描电子显微镜和电子探针观察分析分料盘的磨损机理。
2) distribution disc feeder
分料圆盘
3) singulizing disc
(颗粒燃料元件)分级，分级盘，分类盘
4) drying with tray
料盘干燥
5) packing box
填料盘
1.
chemical compositions analyzing and mechanic performance testing of packing box of hypercompresso
本文主要对超高压压缩机填料盘的材料化学和机械性能进行了测试和研究分
2.
The crack cause in the circle of packing box and the expansion of the crack of the packing box in the thickness and the depth direction,and packing box slippage is only micron degree by internal air pressure effect,with this end in view,the failure of packing box was fretting fatigue and fretting wear.
所有开裂填料盘的裂纹均发生在填料盘圆周方向,并且裂纹是沿着周向和厚度方向扩展的,通过对填料盘受力分析可知,填料盘在内压作用下两相邻填料盘之间的相对滑动量只有微米量级,因此填料盘的失效是由于微动疲劳磨损造成的,从微动疲劳寿命与无微动时拉伸疲劳应力的关系着手,确定影响微动疲劳寿命的因素。
3.
The macrocosmic appearance of the crack of the packing box was analyzed from the creating position and extending direction of crack.
通过对填料盘裂纹产生的部位和裂纹扩展方向的宏观分析,依据微动疲劳裂纹产生的理论,认为填料盘的失效是由于微动疲劳造成的;通过对填料盘工作状况和失效机制的理论分析,进而在理论上证明了填料盘的开裂是由于微动疲劳造成的。
6) spreading plate
撒料盘
1.
Experimental research on spreading plate of swirling classifier;
涡流分级机撒料盘的试验研究
补充资料：三分盘虫
三分盘虫(tribrachidium)
生存年代 _
6亿年至5.8亿年前
生存地点 _
澳大利亚
名称含义 _
“三条小手臂”，它的身体分成三部分，因而得名
这种盘状动物看起来有像海星一样的管足，它也许是海星非常原始的近亲。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条