2) high-speed steel W18Cr4V
高速钢W18Cr4V
1.
TiN coatings were deposited by magnetron sputter ion plating (MSIP) on the surface of high-speed steel W18Cr4V.
通过磁控溅射离子镀方法(MSIP)对高速钢W18Cr4V进行镀TiN膜,采用D/MAX-ⅢB型X射线衍射仪、膜厚测量仪、HV-1000显微维氏硬度计、LKDM-2000型摩擦磨损仪和S-3000N型扫描电子显微镜对经表面改性过的试样组织、膜厚、硬度和耐磨性进行研究,并对镀膜时间、氮分压和溅射电流等工艺参数对TiN涂层的组织、厚度、硬度和耐磨性的影响进行分析。
3) W18Cr4V steel
W18Cr4V钢
1.
W18Cr4V steel was heat-treated by vacuum gas quenching and conventional oil quenching respectively.
采用真空气淬法和普通空气加热油淬法分别对W18Cr4V钢进行热处理。
2.
The performance characteristics of W18Cr4V steel is analysed,and reasonable establishment of forging and heat treatment process of W18Cr4V steel is expounded.
对W18Cr4V钢的性能特点进行了分析,阐述了W18Cr4V钢的锻造及热处理工艺的合理制定。
3.
In this paper, the writer reseached the technology parameter of W18Cr4V steel laser surface quenching.
对W18Cr4V钢激光表面淬火工艺参数进行了试验研究。
4) W18Cr4V alloy steel
W18Cr4V合金刃具钢
5) W6Mo5Cr4V2 high speed steel
W6Mo5Cr4V2高速钢
1.
The influence of cyclic cryogenic treatment on the microstructure and mechanical properties of W6Mo5Cr4V2 high speed steel was studied by XRD,TEM and mechanical properties test.
采用X射线衍射、透射电镜以及力学性能试验等分析方法,研究了多次循环深冷处理对W6Mo5Cr4V2高速钢的显微组织和力学性能的影响。
2.
This paper deals with the influence of conditioning on microstructure and properties of W6Mo5Cr4V2 high speed steel.
研究了预处理工艺对W6Mo5Cr4V2高速钢组织与性能的影响。
3.
The effects of deep cryogenic treatment on the microstructures,mechanical properties and wear resistance of W6Mo5Cr4V2 high speed steel were investigated.
研究了深冷处理对W6Mo5Cr4V2高速钢显微组织、力学性能及耐磨性的影响。
6) H.S.S
高速钢
1.
CONTROL OF INCLUSION DEFECT IN ELECTROSLAG BILLET OF H.S.S.;
高速钢电渣锭夹渣缺陷的控制
2.
TRIAL RESEARCH ABOUT ALLOY-BASE MATERIAL REGENERATED FROM H.S.S. ABRASIVE DUST;
高速钢磨屑再生合金基料的试验研究
3.
QUALITATIVE RESEARCH ABOUT COLORING LAYER ON SURFACE OF ANNEALED H.S.S. WIRE;
退火高速钢线材表面着色层的定性研究
补充资料：W18Cr4V高速钢淬火组织
W18Cr4V高速钢淬火组织