1) stress induced ε M
应力诱发ε_M
2) thermo-induced εM
热诱发ε_M
3) stress induced
应力诱发
1.
The morphology of stress induced ε M in Fe17Mn5Si10Cr5Ni alloy was investigated by Transmission Electron Microscope (TEM) and High Resolution Electron Microscope (HREM).
用透射电镜和高分辨率电镜研究了Fe17Mn5Si10Cr5Ni合金的应力诱发εM形态。
2.
Under a tensile force, the stress induced martensite initially nucleated from the crack tip.
裂纹尖端的应变区未能诱发马氏体形核，而且妨碍了热诱发马氏体的长大在外加拉应力作用下，应力诱发马氏作从裂纹尖端形核后，先形成蝶状马氏体；随后系统中上部也发生了马氏体形核；不同取向的马氏体在长大过程中逐渐转化和合并分析了应变的变化特点，探讨了相变的微观机
4) stress induced εM
应力诱发εM
1.
It was shown that the shape recovery strain decreases rapidly with increasing pre-strain when the deformation is above 5%,although the amount of stress induced εM still increases with increasing pre-strain in the range of 5%.
利用透射电子显微镜对不同变形量试样中应力诱发εM形貌进行观察得知,预应变量由小及大,诱发出的εM形态变化很大,从而对记忆效应产生不同的影响。
5) stress-induced martensite
应力诱发马氏体
1.
The reverse transformation temperature interval of the stress-induced martensite is much sm.
用在(Ms+30℃)温度下的拉伸实验和差示扫描量热仪(DSC)较系统地研究了 Ti44Ni47Nb9 宽滞后形状记忆合金应力诱发马氏体的相变行为。
2.
The results showed that cold rolling process can induce texture of stress-induced martensite and two-way shape memory effect in specific direction.
5Mn合金的双程形状记忆效应的各向异性及其产生机制进行了研究·结果表明,冷轧可造成马氏体织构,且马氏体织构按最大程度缓和外加应力的方式产生,并在特定方向上产生形状记忆效应·通过对压下量的控制,可以在一定范围内任意获得正、负的自发形状变化和热膨胀性·随着加工量的增加,马氏体相变温度区间大幅度扩大·随着温度变化,具有择优取向的应力诱发马氏体晶核的生长和消失是导致可逆的自发形状变化各向异性的根本原因
3.
The reverse transformation temperature interval of the stress-induced martensite was found to be much smaller than that of the thermally induced m.
采用差示扫描量热仪(DSC)系统研究了在(Ms+30℃)温度下拉伸形变对Ti44Ni47Nb9形状记忆合金应力诱发马氏体(SIM)相变行为的影响。
6) stress induced martensite
应力诱发马氏体
1.
The results show that the reverse transformation temperature of stress induced martensite is higher than that of thermal induced martensite and with the increase of deformation the reverse transformation temperature increases.
0 4 9N(质量分数 ,% )合金预应变对应力诱发马氏体相变量及其逆相变温度的影响 。
2.
The volume fraction of stress induced martensite (SIM) in Fe Mn Si Cr N shape memory alloy was determined by X ray diffraction method.
通过 X射线衍射峰位置和强度的计算 ,可以测定 Fe- Mn- Si- Cr- N形状记忆合金中应力诱发马氏体 (ε相 )体积分数 。
3.
The reverse transformation of thermal induced martensite, general stess induced martensite, the stress induced martensite after thermomechanical training in Fe Mn Si based shape memory alloys were studied by an electrostatic audio frequency internal friction instrument.
利用音频内耗仪测试了Ｆｅ－Ｍｎ－Ｓｉ基形状记忆合金热诱发马氏体、一般应力诱发马氏体和热－机械训练后的应力诱发马氏体的逆相变过程。