1) rapld tempering
快速回火
2) high temperature rapid tempering
高温快速回火
1.
A high temperature rapid tempering method was carried out on 40Cr,45 and T10 steels at temperature above Ac1,and compared with the conventional tempering.
采用高温快速回火方法,对40Cr钢及45、T10钢进行了高于Ac1以上温度的高温回火试验,并与传统回火工艺进行了比较,建立了高温回火时间与传统回火温度的对应关系。
3) prompt tempering
快速回火;淬火后立即回火处理;直接回火
4) rapid thermal annealing
快速退火
1.
Effect of rapid thermal annealing on the structure and physical properties of Pt/BST/Pt capacitors
快速退火对Pt/BST/Pt电容器结构和性能的影响
2.
5)TiO_3 thin films were prepared by RF-magnetron sputtering method and crystallized by rapid thermal annealing and conventional furnace annealing.
实验表明:钛酸锶钡薄膜在500℃开始结晶,到700℃左右时结晶比较完善,晶化过程中没有出现择优取向;从表面形貌和X射线衍射图综合分析,快速退火的晶化效果要优于常规退火。
5) high speed ignition
快速点火
1.
Test results indicate that goal of high speed ignition can be attained under the pressure gradient of steepest descent.
试验结果表明，在高减压梯度下可以达到快速点火的目的。
6) rapid annealing
快速退火
1.
The optimum rapid annealing process of high speed steel was given.
分析了退火温度、加热速度、冷却方式等因素对高速钢组织转变特点和结果的影响，提出了高速钢的快速退火最佳工艺，并对Ac1＋（10～20）℃退火与A14＋（10～20）℃快速退火工艺进行了对比。
2.
Compared to conventional annealing regime,rapid annealing by pulse-current heating can obviously improve the magne.
与常规退火工艺相比，脉冲电流加热快速退火，可在保持延性基本不变的情况下，明显改善合金的磁性；是获得非晶态Ｆｅ－Ｂ－Ｓｉ合金磁性优化与良好延性配合的有效途径之
3.
The experimental results showed that the complete transformation from fcc FePt to fct FePt was a-chieved by rapid annealing at 850℃ for 30s.
将化学自组装法制备的FePt薄膜进行快速退火,利用X射线衍射仪和振动样品磁强计对薄膜的结构和磁性进行了研究。