1) organic mud additive
硅氟共聚物
2) fluorosilicone copolymer
氟硅氧烷共聚物
3) Silicon-containing fluorinated acrylate latex
含氟/硅丙烯酸酯共聚物
4) fluorinated siloxane copolymer
氟化硅氧烷共聚物
6) fluorosilicone
[,flu:ərə'silikəun]
氟硅聚合物
1.
From poly(methylhydrosiloxane),organofluorine,allyl polyoxyethylene polyoxypropylene ether,and siliane coupling agent,a series of waterbased fluorosilicone were synthesized via hydrosilation at 85~90 ℃ for 3.
采用硅氢加成法在无溶剂的条件下,将烯丙基聚氧乙烯聚氧丙烯醚,含氟单体及硅烷偶联剂与低含氢硅油发生接枝共聚,成功地制备了一系列有机氟硅聚合物。
2.
01%) of the raw material weight,a series of water-based fluorosilicone were synthesized by using poly(methylhydrosiloxane),organoflurine,allyl polyoxyethylene polyoxypropylene ether,and silicane coupling agent.
01%以及无溶剂的条件下,采用硅氢加成法将烯丙基聚氧乙烯聚氧丙烯醚、含氟单体及硅烷偶联剂与低含氢硅油进行接枝共聚,成功地制备了一系列有机氟硅聚合物。
3.
Without solvent, a series of water-based fluorosilicone polymers were synthesized from allyl polyoxyethylene polyoxypropylene ether, organic fluoride and poly(methylhydrosiloxane) via hydrosilyla- tion, and the aqueous dispersions of the polymers were obtained by the way of emulsification.
在无溶剂的条件下,通过硅氢加成法将烯丙基聚氧乙烯聚氧丙烯醚,氟化丙烯酸烷基酯接枝共聚到甲基含氢硅油侧链,成功地合成了一系列有机氟硅聚合物。
补充资料：氯乙烯和乙烯僧酸乙烯共聚物接枝共聚物
分子式：
CAS号：
性质：为在乙烯/醋酸乙烯共聚物(EVA)之大分子链上进行氯乙烯接枝共聚后得到之产品，按EVA中醋酸乙烯含量不同和接枝共聚物中EVA含量不同以及分子量大小，分为冲击改性剂用、硬质和软质品用三类。作冲击改性剂用和软质品用者多为EVA中VAC含量45％，EVA含量为50％。主要用于防水卷材、医用制品、电缆、记录材料和与PVC共混后作门窗型材。硬质品用者为EVA中VAC含量为15％，EVA含量5％～10％。除接枝物外含聚氯乙烯均聚物。可直接用作门窗型材和管材，冲击强度比一般PVC可提高4倍以上，将EVA溶于或分散于氯乙烯单体中进行悬浮聚合制得。
CAS号：
性质：为在乙烯/醋酸乙烯共聚物(EVA)之大分子链上进行氯乙烯接枝共聚后得到之产品，按EVA中醋酸乙烯含量不同和接枝共聚物中EVA含量不同以及分子量大小，分为冲击改性剂用、硬质和软质品用三类。作冲击改性剂用和软质品用者多为EVA中VAC含量45％，EVA含量为50％。主要用于防水卷材、医用制品、电缆、记录材料和与PVC共混后作门窗型材。硬质品用者为EVA中VAC含量为15％，EVA含量5％～10％。除接枝物外含聚氯乙烯均聚物。可直接用作门窗型材和管材，冲击强度比一般PVC可提高4倍以上，将EVA溶于或分散于氯乙烯单体中进行悬浮聚合制得。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。