1) blowing bottle
吹塑瓶
1.
The causes and countermeasures of explosion and leakage of PET blowing bottles for drink are analyzed.
分析了碳酸性饮料用PET吹塑瓶爆裂、渗漏的原因及其对策,该分析方法也适用于其它PET吹塑制品。
2.
The influence of such factors as temperature, pressure and molds on the product quality in the molding process of PET blowing bottle was inquired.
探讨了PET吹塑瓶成型工艺中温度、压力及模具等因素对制品质量的影响。
2) plastic bottle-blower
塑料吹瓶机
3) push-ups
[英]['puʃʌp] [美]['puʃ,ʌp]
内凹底<吹塑瓶>
4) neck area (of blow mo(u)ld)
瓶颈区(吹塑模)
6) blow molding
吹塑
1.
The increase of crystallite size and notable changes of orientation factor for crystal planes during blow molding process reveale.
利用DSC和W AXD研究了医用聚丙烯专用料(TPC)及其密封式直立吹塑瓶(TPCC)的熔融行为和结晶结构。
2.
The barrier property of the container made by the blow molding is excellent.
研究结果表明,MST含量约为10％时,可以得到综合性能优于尼龙6的可吹塑高阻隔性的材料,该材料可以用作汽车燃油箱、农药瓶、药品瓶等有高阻隔性要求的包装材料的专用料,具有广阔的应用前景。
3.
Recent progress in materials, equipment, process and products of blow molding was reviewed.
对近年来中空吹塑在材料、设备、工艺和制品方面的进展进行了总结。
补充资料：拉伸对PET瓶吹塑成型的影响
随着塑料中空成型技术的快速发展，PET瓶吹塑工艺也越来越先进、实用。拉伸吹塑法就是这样一种先进、实用的工艺。本文以日本日精公司注-拉-吹一步法PET瓶成型机为例来讨论拉伸在PET瓶吹塑过程中的作用。
拉伸过程
拉伸实际是高分子链在玻璃化温度
以上（熔点以下）在外力作用下发生的定向作用。紧随拉伸动作之后的吹涨实际也是双向拉伸作用。
拉伸与成型效果
经过拉伸、吹塑的瓶子，其壁厚均匀性更佳，由于快速进行的竖向拉伸，保证了“底厚壁薄”的技术要求，瓶颈处再也没有“积料现象”。但如果瓶坯预热不充分，或吹瓶模冷却效果差，也会造成很大偏差。
由于定向以及因定向而使分子链间吸引力增加，拉伸后经过冷却定型的瓶壁的抗张强度、拉伸强度、抗冲强度都有很大的提高，这些对产品在堆垛、运输过程中的安全性很有作用。
经过拉伸后，由于分子链作定向、近乎规整的排列，反映在瓶壁外观上是光泽增加，透明度增加。
拉伸吹塑过程的注意事项
一﹒ 要生产出透明性好的PET瓶，拉伸速度要快，只有在玻璃化温度以上偏低温（95度左右）下使瓶坯迅速拉伸定向，才能提高制品瓶的拉伸强度和冲击强度。
二﹒ PET在拉伸吹塑过程中，加热温度范围窄，温度过高或过低均会使瓶身出现混浊，因此，在瓶坯加热过程中，瓶坯整体温差要小，要均匀，加热温度要控制准确，最好采用远红外加热，因为它具有穿透性。
三﹒ 吹塑用的压缩气必须预处理，除去其中的水份和油份，以免在瓶内壁上留下麻点，影响透明性或卫生。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。