1) crazing temperature of brittleness
脆性开裂温度
2) brittle fracture
脆性开裂
1.
In the light of the cracking accidence of the welding structure of a large type excavator used in the mine, this paper studies on the dynamic fractu re characters of 15MnV steel through simulating the actual working condition, an d analyzes on the reasons of the occurrence of the brittle fracture.
针对某矿山用大型挖掘机焊接结构构件的开裂事故,模拟实际工况研究了15MnV钢的动态断裂特性,分析了产生脆性开裂的原因。
4) brittleness temperature
脆性温度
1.
The minimum brittleness temperature of the ACM filled with DOP was -38 and which filled with DBS was -42.
并用IR、1H-NMR表征了共聚物的结构;DMTA测定共聚物的玻璃化转变温度(Tg);填充邻苯二甲酸二辛酯(DOP)的丙烯酸酯橡胶的最低脆性温度达-38℃;填充癸二酸二丁酯(DBS)的丙烯酸酯橡胶的最低脆性温度达-42℃。
5) low ductility region
脆性温度区
1.
It is found that the low ductility region Ⅲ is between 920 and 730 ℃.
为了研究残余元素Cu、As和Sn对钢高温延塑性的影响,采用Gleeble-1500热模拟试验机测试了含有一定量Cu、As和Sn低合金钢连铸坯的高温延塑性,得到了低合金钢第Ⅲ脆性温度区在920～730℃之间。
2.
It was found that the low ductility temperature regionⅠof low alloy steel was between ts and 1340 ℃ and the low ductility region Ⅲ was between 920-730 ℃.
低合金钢的第Ⅰ脆性温度区在ts~1 340℃之间,第Ⅲ脆性温度区在920~730℃之间。
6) embrittlement rupture temperature
脆化断裂温度
1.
The rheology property and embrittlement rupture temperature of the production were studied.
以再生丁基橡胶为主体材料研制密封胶条,通过正交试验方法安排实验,考察产品的流变性能和脆化断裂温度,讨论不同原料对产品性能影响的主次关系,选定最优配方。
补充资料：耐低温开裂温度
分子式：
CAS号：
性质：在低温下将试样猛烈地弯折而不产生开裂的最低温度。这是高分子材料在低温使用条件下的一种实用检验，有相应的试验方法规定具体的试验条件。有一个测定软塑料片的低温对折冲击试验就是将试样对折后夹在试想样夹上，然后浸入酒精干冰的冷媒内，恒温后用一定能量的冲锤冲击试样，求其破裂率为50%时的温度。
CAS号：
性质：在低温下将试样猛烈地弯折而不产生开裂的最低温度。这是高分子材料在低温使用条件下的一种实用检验，有相应的试验方法规定具体的试验条件。有一个测定软塑料片的低温对折冲击试验就是将试样对折后夹在试想样夹上，然后浸入酒精干冰的冷媒内，恒温后用一定能量的冲锤冲击试样，求其破裂率为50%时的温度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。