1) foaming mechanism
发泡机理
1.
A study on foaming mechanism of thermovulcanizated silicone sponge compound;
热硫化型硅橡胶海绵发泡机理浅析
2.
Its foaming mechanism is that Some gas, given off from foaming agents, was closed and formed many small bubbles in the brick of foam glass due to sintering.
其发泡机理是 :发泡剂放出的气体一部分由于烧结被包裹在坯体中形成微小气泡 ,当温度升高至发泡温度、玻璃软化时 ,气泡膨胀 ,坯体体积增大而成为泡沫玻璃。
3.
Foam glass was prepared with sintered process, using moderate amount of additives and the powder of waste stiff glass fiber as main material and its foaming mechanism was investigated.
以废玻璃纤维硬丝为主要原料 ,添加适量外加剂 ,采用烧结法制备出质量符合要求的泡沫玻璃 ,并探讨了其发泡机理 。
2) mechanism of micro-cellular foaming
微发泡机理
3) physically foaming
物理发泡
1.
Design & production of physically foaming coaxial cable for distribution systems;
电缆分配系统用物理发泡同轴电缆的设计与制造
2.
The self-made gas-supplying apparatus is used to inject supercritical CO_2 into conventional physically foaming extruder instead of N_2,and the foaming properties of LDPE,HDPE,and ADD blending system are studied.
利用自行研制的供气装置将超临界CO2注入普通N2物理发泡挤出装置,并对LDPE,HDPE,ADD的共混体系的发泡性能进行了应用研究。
4) physical foaming
物理发泡
1.
The foaming period of modified method (MM) was less than that of conventional physical foaming(PF).
介绍了制备开孔硅橡胶泡沫的一种独特方法 ,该方法的工艺时间比传统的物理发泡时间短 ,具有更强的可操作性 ,减少了物理发泡剂的浪费 ,制备的泡沫开孔率与普通物理发泡的开孔型泡沫相当 ,与化学发泡制备的开孔型泡沫相比 ,泡孔细小均匀 ,且具有较小的压缩永久变形 (4 %～ 6 %
2.
Hydroxyapatite/collagen protein porous scaffolds were prepared with hydroxyapatite powders mixed with collagen protein,via physical foaming,freezing and micro-wave drying.
把羟基磷灰石粉与一定量的胶原蛋白溶液混合,经过物理发泡、冷冻、微波干燥的过程,得到羟基磷灰石/胶原蛋白多孔支架材料。
5) polyurethane foaming machine
发泡机
1.
Temperature field analysis of seal contact surface in the mixer of polyurethane foaming machine;
聚氨酯发泡机混合器密封接触面的温度场分析
2.
A new mixer is designed,which is used in polyurethane foaming machinel.
设计了一种新型的低压聚氨酯发泡机混合头,采用两步搅拌以及隔离发泡剂技术,解决了传统发泡机混合头存在搅拌不均匀以及容易堵塞等问题。
6) foaming mechanism
发泡机制
1.
The foaming mechanism of AFS through the rolling-bonding process was found preliminarily.
研究了轧制复合-粉末冶金发泡法制备泡沫铝夹心板的生产工艺,分析了板/芯结合工艺对芯层粉末致密度的影响,探讨了粉末致密度与发泡效果间的关系,初步得到了复合板的发泡机制。
2.
But the basic theories producing porous metals in high temperature were not yet fully understood, especially the foaming mechanism, foaming thermo-dynamics study on nucleation, growth, movement and rupture of gas bubble were rarely researched.
但是对于发泡过程基础理论研究还不够全面，特别是气孔的发泡机制即气孔在基体金属内随外界条件变化而发生的形核、生长、运动和消亡等热、动力学条件的研究很少。
补充资料：变压发泡技术（VPF）
变压发泡技术（VPF）。在软质聚氨酯泡沫生产中。通过控制发泡环境压力，不用任何辅助发泡剂就能生产各种密度的泡沫制品的技术称为变压发泡技术。变压发泡技术生产的泡沫密度范围一般在10-80kg/m3，工作压力控制在-0.05-0.05MPa(表压)。该技术最初应用于软泡连续生产线，通过分段控制，周期切换密闭的成型通道内系统压力，从而实现水平连续发泡。美国Foamex公司作为使用方与英国设备制造商Beamech公司合作开发的变压发泡连续生产线已成功使用多年。由于该设备体积庞大，控制系统复杂，因而价格较高。采用变压发泡连续生产线，生产规模应在1万吨/年以上。该设备优点是连续生产、产量大、效率高、生产中产生的头尾泡沫占总体泡沫比率小，原料利用率高。近年来该技术已经扩展至间歇变压(VPF)箱体法，与变压发泡连续生产线相比，间歇式设备大大简化，投资不大，缺点是产量较低。国外OMs公司、Beamech公司、Hnnecke公司均有间歇箱体变压成套设备出售。北京福奥盟化工技术有限公司2003年开发研制了此类设备，现已商品化。国内尚有数家企业正在研制半连续聚氨酯软质泡沫真空发泡生产线设备，有的已投料试车，试制设备箱体长度一般为60m以上，为了减少头尾泡沫占总体泡沫比例，有加长箱体的趋势。该类设备与原普遍使用的水平生产线设备有很多相同之处，泡沫截面尺寸也基本相同，主要区别在于箱体内耍保持一定的负压。这类没备产量较大，适合一般生产厂家要求，但头尾泡沫占总体泡沫比例较大，原料利用率偏低。