1) hot dip galvanizing
热浸镀Zn
2) Hot-dip Zn-Ni alloy
热浸镀Zn-Ni合金
3) hot dipping
热浸
1.
The hot dipping alumetizing technology for 20G seamless steel tube was studied.
对 2 0 G无缝钢管的热浸渗铝工艺进行了研究和试验。
2.
This paper describes the selection of the flux used in hot dipping aluminizing and the process.
采用金相、扫描电镜、电子探针及x射线衍射等现代测试技术分析渗层成分及相组成,结果表明,以复合氯化物水溶液为助镀剂对钢材进行热浸渗铝,渗铝层由α-Fe(Al)固溶体,Fe_2Al_5及纯铝层构成。
4) hot dipping
热浸镀
1.
Research on the material of hot dipping pot for 55% Al-Zn alloy layer;
应用于热浸镀55%铝锌合金锅体材料的研究
2.
This paper dealt with some of hot dipping 55%Al-Zn fluxes for un-hardened and tempered N80 steel.
研究了石油管常用材质非调质N80钢热浸镀55%Al-Zn合金的助镀工艺,确定了最佳助镀方法为电解活化加浸4%K2ZrF6水溶液的助镀法。
5) hot-dip aluminized steel
热浸铝钢
6) hot-dip
热浸镀
1.
The application of grey model GM(1,1) in the research of sea-water corrosion resistance of hot-dip coatings;
灰色GM(1,1)模型在热浸镀层耐海水腐蚀研究领域的应用
2.
Effect of Ti addition on hot-dip zinc coating;
添加钛元素对热浸镀锌层性能的影响
3.
The Influence of Diffusion Annealing on the Organization of Hot-dipped Aluminum Coating on the Ductile Iron;
扩散退火对球墨铸铁热浸镀铝组织的影响
参考词条
补充资料：热浸镀
分子式：
CAS号：
性质：又称熔融镀（fuse dipping）。将工件浸入熔融的金属液中，以获得金属镀层的过程。能用于热浸镀的金属只是熔点较低的金属及其合金。如锡、锌、铝、铅锡合金等。基体材料一般是钢铁，有时也用铜。浸镀前工件需进行表面预处理，清除表面的油污和氧化皮。热浸镀后还要进行化学处理、涂油或必要的整形。热浸镀的优点在于得到的镀层较厚，能在较恶劣的环境中长期使用。如用于高速公路的护栏、桥梁和建筑材料。但浸镀层厚度和均匀性不易控制，外观也不如电镀层好。优点是：（1）操作和设备简单；（2）效果比电镀好。缺点是：（1）覆盖层较厚；（2）不规则的制件不容易形成均匀的膜；（3）只适于用低熔点金属（锌、锡、铝、铅）覆盖。
CAS号：
性质：又称熔融镀（fuse dipping）。将工件浸入熔融的金属液中，以获得金属镀层的过程。能用于热浸镀的金属只是熔点较低的金属及其合金。如锡、锌、铝、铅锡合金等。基体材料一般是钢铁，有时也用铜。浸镀前工件需进行表面预处理，清除表面的油污和氧化皮。热浸镀后还要进行化学处理、涂油或必要的整形。热浸镀的优点在于得到的镀层较厚，能在较恶劣的环境中长期使用。如用于高速公路的护栏、桥梁和建筑材料。但浸镀层厚度和均匀性不易控制，外观也不如电镀层好。优点是：（1）操作和设备简单；（2）效果比电镀好。缺点是：（1）覆盖层较厚；（2）不规则的制件不容易形成均匀的膜；（3）只适于用低熔点金属（锌、锡、铝、铅）覆盖。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。