1) peptization-hyedrolysis method
溶胶水解法
2) hydrolysis-sol
水解-溶胶法
3) hydrolytic sol-gel
水解溶胶-凝胶法
1.
Aluminum titanate powder was synthesized by nonhydrolytic and hydrolytic sol-gel method,respectively.
分别采用非水解和水解溶胶-凝胶法合成钛酸铝粉体,利用FT-IR、DTA-TG、XRD、SEM等方法研究了溶胶-凝胶转变和合成相变化过程及粉体烧结性能。
4) sol-hydrolysis
溶胶水解
5) non-hydrolytic sol-gel
非水解溶胶-凝胶法
1.
Porous TiO_2 photocatalytic thin films were prepared by the non-hydrolytic sol-gel route.
采用非水解溶胶-凝胶法制备了多孔TiO_2光催化薄膜。
2.
TiO_2 photocatalytic thin films were prepared by the non-hydrolytic sol-gel method using TiCI4 as precursor,absolute etha- nol as oxygen donor and polyethylene glycol (PEG) as film-forming agent.
以TiCl_4为前驱体,无水乙醇为氯供体,聚乙二醇(polyethyleneglycol,PEG)为成膜控制剂,通过非水解溶胶-凝胶法制备了TiO_2光催化薄膜。
3.
zircon has been synthesized by the non-hydrolytic sol-gel route using zirconium tetrachloride and tetraethoxysilane as precursors.
以工业纯ZrCl4、Si(OC2H5)4为前驱体,通过非水解溶胶-凝胶法合成了硅酸锆。
6) nonhydrolytic sol-gel
非水解溶胶-凝胶法
1.
Aluminum titanate gel is prepared by nonhydrolytic sol-gel route using titanium tetrachloride and anhydrous aluminum trichloride as precursors and anhydrous alcohol as an oxygen donor.
以无水三氯化铝和四氯化钛为前驱体,以无水醇为氧供体通过非水解溶胶-凝胶法制备钛酸铝凝胶。
2.
Aluminum titanate powder has been synthesized at low temperature of 750℃bysolvent-free nonhydrolytic sol-gel route using titanium tetrachloride and anhydrousaluminum trichloride as precursors and anhydrous alcohols as oxygen donors.
本研究采用无水低碳醇为氧供体，以无水AlCl_3和TiCl_4为前驱体，利用无溶剂的非水解溶胶-凝胶法在750℃低温合成出钛酸铝粉体。
补充资料：低压压热釜油脂水解法
分子式：
CAS号：
性质：早期常用的油脂水解工艺方法。油脂和水在压热釜中通入压力为1MPa的饱和蒸汽。温度达到该压力下的饱和温度(约180℃)。由于在此温度下水在油脂中的溶解度不够，要加入碱性催化剂，一般用钙、镁或锌的氧化物，以氧化锌较普遍。其实质是第一步生成上述碱土金属的皂，金属皂使油脂与水形成油包水型乳液。在上述条件下反应时间为10h左右，分批进行，分解率可达95％。当原料质量好时，所得的脂肪酸色泽浅，不经蒸馏即可直接用于制皂或其他产品。
CAS号：
性质：早期常用的油脂水解工艺方法。油脂和水在压热釜中通入压力为1MPa的饱和蒸汽。温度达到该压力下的饱和温度(约180℃)。由于在此温度下水在油脂中的溶解度不够，要加入碱性催化剂，一般用钙、镁或锌的氧化物，以氧化锌较普遍。其实质是第一步生成上述碱土金属的皂，金属皂使油脂与水形成油包水型乳液。在上述条件下反应时间为10h左右，分批进行，分解率可达95％。当原料质量好时，所得的脂肪酸色泽浅，不经蒸馏即可直接用于制皂或其他产品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条