Optimization conditions of preparation of high solid loading ceramic slurries are investigated by ways of powder surface modification,some better technique ways of powder surface modification being intruduced,and problems at present time are pointed.
从粉体表面改性的方面对高固相含量碳化硅陶瓷料浆的制备工艺进行了研究 ,介绍了一些陶瓷粉体表面改性方法 ,并指出了存在的问题 。
2.
In this paper, optimization conditions of preparation of high solid loading ceramics slurries are in vestigated by ways of powder sulface modification and uses of dispersant, some better technique ways of powder surface modification being intruduced,uses of dispersant being disscussed, and problem at present time are pointed.
通过从粉体表面改性和分散剂的使用两方面对高固相含量料浆的制备工艺进行了研究，介绍了一些陶瓷粉体表面改性方法，讨论了分散剂的作用，并指出了存在的问题。
2) surface modification of powder additive
粉体助剂表面改性
4) α-Al2O3 micro-powder surface modification
Al_2O_3微粉表面改性
5) α-Al_2O_3 micropowder surface modification
Al2O3微粉表面改性
6) The surface modification and application of the zirconia series powders
锆系粉体表面改性及应用
补充资料：增强体表面处理
分子式：
CAS号：
性质：复合材料中的增强体与基体是性质不同的两种物质，它们在复合材料中通过界面互相连接。使增强体与基体产生良好的界面规格的条件是：(1)基体与增强体之间能充分润湿，紧密接触；(2)基体与增强体之间形成键；(3)界面处的基体在固化时对增强体产生压缩压力。为了达到上述条件必须对增强体表面用化学的或物理的方法进行处理。由于增强体表面性质不同，处理的方法不同。如对玻璃纤维可用偶联剂处理，对碳纤维可采用涂层法、氧化法、净化法、溶液还原法及冷等离子法处理，对芳纶纤维可用等离子体，表面化学法、表面高聚物涂层等方法处理。
CAS号：
性质：复合材料中的增强体与基体是性质不同的两种物质，它们在复合材料中通过界面互相连接。使增强体与基体产生良好的界面规格的条件是：(1)基体与增强体之间能充分润湿，紧密接触；(2)基体与增强体之间形成键；(3)界面处的基体在固化时对增强体产生压缩压力。为了达到上述条件必须对增强体表面用化学的或物理的方法进行处理。由于增强体表面性质不同，处理的方法不同。如对玻璃纤维可用偶联剂处理，对碳纤维可采用涂层法、氧化法、净化法、溶液还原法及冷等离子法处理，对芳纶纤维可用等离子体，表面化学法、表面高聚物涂层等方法处理。