1) epoxy resin concrete
环氧树脂混凝土
1.
Study on epoxy resin concrete and its application to engineering;
环氧树脂混凝土的研究现状和工程应用
2.
Partial treatment of turbogenerator foundation with epoxy resin concrete;
用环氧树脂混凝土对汽轮机基础进行局部处理
3.
Study on pavement performance of epoxy resin concrete
环氧树脂混凝土路用性能研究
2) epoxy concrete
环氧树脂混凝土
1.
This paper discusses the patterns and the phase boundaries of rubber domains in the modified epoxy concrete under the various technological conditions, by meansof changing the solidification processes and using the method of micro-phase analysis.
通过改变固化工艺，采用显微图相分析手段，探讨了改性环氧树脂混凝土中橡胶分散相在不同工艺条件下的形态和相界面。
3) Resin Concrete
树脂混凝土
1.
The Analysis and Optimization of Machine Tool Bed with Resin Concrete;
树脂混凝土床身结构动态分析与优化
2.
Research of making resin concrete by coal gangue and fly ash;
大掺量煤矸石和粉煤灰制备树脂混凝土的研究
3.
Tentative study on the seismic behavior of special-shaped columns frame fast repaired with the resin concrete;
树脂混凝土快速修复异形柱框架试验研究
5) furan resin concrete
呋喃树脂混凝土
1.
Firstly,the experiment performed about the bending and creep characteristic of non-FRP reinforced furan resin concrete beam and FRP reinforced furan concrete beam,and the creep curves of the beams under different loads were gained by four-point bending test method.
首先对呋喃树脂混凝土梁和FRP筋加强呋喃树脂混凝土梁的弯曲蠕变特性进行了试验研究与分析,采用四点弯曲试验方法分别得到了梁在不同荷载水平作用下的蠕变曲线,对其粘弹性性质进行了分析。
6) resinification concrete
树脂化混凝土
补充资料：二氧化双环戊二烯环氧树脂
分子式：
CAS号：
性质：又称R型环氧树脂。双环戊二烯的二氧化物。白色结晶粉末，分子量164.2，相对密度1.330，熔融温度≥185℃，环氧当量82。易溶于乙酸、醇、醚、酮、苯、四氯化碳等。固化物马丁耐热200℃以上，耐候性及电性能好，硬度高，有自熄性。缺点是冲击性能欠佳。由双环戊二烯与过醋酸反应而得。可铸塑、模塑和层合。主要用作耐热、耐候铸塑料、模塑料、玻璃钢、胶黏剂和涂料。
CAS号：
性质：又称R型环氧树脂。双环戊二烯的二氧化物。白色结晶粉末，分子量164.2，相对密度1.330，熔融温度≥185℃，环氧当量82。易溶于乙酸、醇、醚、酮、苯、四氯化碳等。固化物马丁耐热200℃以上，耐候性及电性能好，硬度高，有自熄性。缺点是冲击性能欠佳。由双环戊二烯与过醋酸反应而得。可铸塑、模塑和层合。主要用作耐热、耐候铸塑料、模塑料、玻璃钢、胶黏剂和涂料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。