1) oxalate gel coprecipitation
草酸胶态沉淀法
2) gel oxalate precipitation
草酸盐胶态共沉淀
4) oxalate coprecipitation method
草酸盐共沉淀法
1.
BaTiO3 powder was synthesized by oxalate coprecipitation method,and through the experiment and characterizations of XRD,DTA-TG,IR,TEM the result indicated that the product BaTiO3 was cube,well-proportioned and the size was about 30nm and reunited less.
利用草酸盐共沉淀法合成BaTiO3纳米粉体,通过XRD分析、DTA-TG分析、IR分析及TEM形貌分析等分析手段,对制得的粉体进行了表征和测试,结果表明合成的BaTiO3粉体为单纯的立方相,粒径均匀,颗粒大小在30 nm左右,无严重的团聚现象。
2.
In order to develop more effective,nontoxic and environment-friendly inorganic luminescent nanomaterials for manifesting fingerprint,the Eu3 + doped LaPO4 nano-materials were synthesized by oxalate coprecipitation method.
为了研究新型高效的、对人体无毒、对环境无污染的显现指印的无机纳米荧光材料,采用草酸盐共沉淀法制备纳米发光材料LaPO4∶Eu3+,并利用PAMAM树形分子配置LaPO4∶Eu3+/PAM-AM G5。
5) precipitation method of oxalate
草酸盐沉淀法
1.
Ultra fine LaPO_4∶Eu powder was prepared by precipitation method of oxalate.
采用草酸盐沉淀法制备超微发光粉体La-PO4∶Eu。
6) oxalate coprecipitation
草酸共沉淀法
1.
The giant dielectric constant material CaCu3Ti4O12(CCTO) powder has been fabricated successfully by an oxalate coprecipitation method.
用草酸共沉淀法在700℃保温1 h制备出了单相CaCu3Ti4O12粉体。
补充资料：胶状沉淀
分子式：
CAS号：
性质： 胶体的粒子一般直径小于0.02μm。当胶粒聚集时，得到的是含有大量水分的胶状沉淀。该沉淀体积大、疏松，不易过滤。用纯水洗涤沉淀时易胶溶，穿透滤纸。一般条件下，高价金属的氢氧化物沉淀，大都属于胶状沉淀类型。
CAS号：
性质： 胶体的粒子一般直径小于0.02μm。当胶粒聚集时，得到的是含有大量水分的胶状沉淀。该沉淀体积大、疏松，不易过滤。用纯水洗涤沉淀时易胶溶，穿透滤纸。一般条件下，高价金属的氢氧化物沉淀，大都属于胶状沉淀类型。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条