1) chlorine leaching process
氯气浸出法
2) chlorine leaching
氯气浸出
1.
The process of chlorine leaching-purification-eletrowinning for nickel extraction from copper residue is investigated.
研究通过氯气浸出-净化-不溶阳极电积法生产电镍的工艺过程。
2.
The flow sheet consists of alkali roast-leaching by NaOH solution-chlorine leaching-removing iron by TBP solvent extraction-removing chromium by hydrolyzing-removing other impurities by P204 solvent extraction-separating nickel from cobalt by N235 solvent extraction.
研究了采用"苏打焙烧—碱浸出铝、钼—氯气浸出钴、镍、铁等—TBP萃取除铁—中和水解除铬—P204萃取除微量杂质—N235萃取分离镍、钴"工艺处理废高温镍钴合金,重点考察了从废镍钴合金中浸出镍和钴,讨论了苏打焙烧温度和碱浓度对铝、钼浸出率的影响,碱浸渣氯气浸出电位、浸出时间、废合金粒度、添加剂的加入等因素对镍、钴浸出率的影响。
3) chlorine leaching solution
氯气浸出液
1.
In light of the composition of chlorine leaching solution of nickel concentrate, i.
本试验研究了针铁矿法从镍精矿氯气浸出液中除铁的工艺 。
4) chlorination leaching
氯化浸出
1.
A new technigue for copper electrolysis of Au-Cu ore with chlorination leaching electrolyte in a diaphragm cell;
金铜矿氯化浸出隔膜电解新工艺
2.
A new Au-Ag recovery process,"additives roasting-chlorination leaching-reduction by sodium sulfite" for the complex gold flotation concentrate is described in this article.
介绍了采用"添加剂焙烧—氯化浸出—亚硫酸钠还原"工艺从某浮选含碳砷、高硫金精矿提取金银的试验过程和结果,该方法不仅克服了传统氰化法的流程长、劳动强度大、成本高等缺点,也克服了其它化学湿法回收贵金属高污染的缺点,而且回收率高,生产周期短,劳动条件较好,能综合回收有价金属。
3.
In the chlorination leaching solution of Shizhuyuan complex bismuth concentrate bearing beryllium and fluorine,there were more than forty species which were coordinated with metal ions,such as Bi 3+ ,Be 2+ ,Fe 3+ ,and ligands such as Cl -,F - and SO 2- 4,respectively.
柿竹园含铍含氟铋精矿成分十分复杂，其氯化浸出液中铋、铍、铁等分别与配位体Ｃｌ－，Ｆ－，ＳＯ２－４形成配合物，物种多达４０余种。
5) chloridizing leaching
氯化浸出
1.
The synthesis of sodium antimonate from antimony concentrates by chloridizing leaching-oxidation and hydrolysis decomposition-alkali synthesis process is investigated.
研究以辉锑精矿为原料、经氯化浸出-氧化-水解-加碱合成制取焦锑酸钠的工艺。
6) Chloride Leaching
氯盐浸出
1.
The Thermodynamical Analysis of Chloride Leaching Bismuth Sulphide;
含铋硫化物氯盐浸出的热力学分析
2.
Using Cu~(2+) as oxidazing angent and neutral chloride as complexing angent, the oxidation chloride leaching kinetics of low-grade bismuth sulphide ore is studied.
结果表明,硫化铋矿的氯盐浸出符合缩小未反应核模型;在实验条件下,铋的溶解速率遵循直线规律。
补充资料：氯气选择浸出富集铂族金属
氯气选择浸出富集铂族金属
concentration of platinum group metal by chlorine selective leaching
!Uqi xuanze iinehu fuJ!bozu Jinshu抓气选择漫出富集铂族金属(coneentrationof platinum group metal by chlorine seleetiveleaching)往水溶液或稀盐酸溶液中通氯气溶出含铂族金属物料中的贱金属，使铂族金属留在浸出渣中而得到富集的过程。此法可用以处理铜镍冶金过程中产出的各种含贵金属中间产物，如高镍梳、铜镍合金、电解阳极泥等。也可用于处理废杂物料回收产出的含贵金属混合物料。该法对原料适应性强，生产规模可小可大，设备生产率高，分离贱金属的效果好，能耗低，是铂族金属富集的重要方法。 原理氯气是强氧化剂，它在水或盐酸溶液中可氧化溶解贵贱金属。但铜、镍、铁、钻等贱金属的标准电极电位比贵金属负得多，利用金属标准电极电位的差异，选择一个能溶解贱金属而不能溶解贵金属的电极电位值范围，就可使贵贱金属分离。采用由铂电极和甘汞电极组成的电极对插入溶液，用电位计测定浸出矿浆的电极电位。在选择浸出过程中，通过调整抓气或物料供给量，将矿浆的电极电位控制在400mV士10mv范围(见图).在此电极电位范围内，贱金属(Me)便和抓气作用生成可溶性氯化物转人溶液，反应为: Me+C12—MeC12 MeS+C12—MeC12+50而贵金属则不和抓气作用残留在浸出残渣中得到富集。选择浸出的电极电位偏低，贱金属浸出率不高;偏高，则贵金属会发生溶解损失。 应用20世纪70年代加拿大鹰桥镍矿业公司100r-esesesesesesesesesTes，rr 80卜I}’} 次l户l}} 介60卜砚犷声.、沐山行‘、} 几40卜/}r{ 2”{.…，洲 300 400 500 电位V/mV 氛气选择浸出分离贵、贱金属的电极电位范围 (铂一甘汞电极)(Faleonbridge Nieel Mines Ltd.)精炼厂曾用该法处理高镍铣盐酸浸出镍后的铜渣(含Cu76%、Nil%、铂族金属和金0.5%)，作法是铜渣料先用含Cu2+sog/L、NiZ+1009/L、HC15og/L的溶液浆化，然后通入氯气，浸出体系的电极电位控制在400mV土lomV浸出贱金属。贵金属富集在过滤后以元素硫为主要成分的浸出渣中，品位富集4一5倍。 80年代用氯气直接浸出高镍梳，贵金属也能富集4一5倍。中国金川有色金属公司用此法处理高镍梳磨浮磁选出的铜镍合金，铜镍合金的成分(质量分数。/%)为:Ni 60~70，Cu 15一19，Fe7~8，56~8，铂族及金0.01。