1) hypereutectoid steel (T10A)
过共析钢(T10A)
2) T10A Steel
T10A钢
1.
WEDM Crackle Analysis and Their Technical Improvement of the T10A Steel Mould;
T10A钢模具线切割裂纹的分析与工艺改进
2.
By means of high temperature microscope,graphite precipitation from T10A steel specimens with 4 kinds of original structures has been dynamicly observed when heated and cooled in vacuum.
用高温金相显微镜动态观察4种原始组织的T10A钢试样在真空加热及冷却时的石墨析出现象。
3.
Effects on 45 & T10A steel in different process time of salt-bath chromizing adding rare-earth were studied.
在相同温度下,对45钢和T10A钢进行不同时间的稀土盐浴渗铬,结果表明:随着渗铬时间的延长,渗铬的效果,在总体上呈增加的趋势,45钢在4h就可以达到较好效果,而T10A钢则在6h达到较好效果。
3) hypereutectoid steel
过共析钢
1.
Ultra-refinement of hypereutectoid steel during deformation of undercooled austenite;
过共析钢在过冷奥氏体形变过程中的组织超细化
2.
Effect of processing parameters on dynamic transformation of undercooled austenite of hypereutectoid steel
工艺参数对过共析钢过冷奥氏体动态转变的影响
3.
In order to detect the carbide network in high carbon hypereutectoid steel wire rods accurately,two kinds of detection method of the carbide network are compared.
为了准确地检验高碳过共析钢盘条中的网状渗碳体,分别对选用硝酸酒精溶液侵蚀和碱性苦味酸钠水溶液热侵蚀两种显示方法进行了比较。
4) T10A specimen
T10A钢试样
5) T10A tool steel
T10A工具钢
6) Hype-eutectoid
过共释钢
补充资料：过共析钢
分子式：
CAS号：
性质：含碳量高于0.77%的碳素钢。显微组织有珠光体和先析渗碳体。该渗碳体沿原奥氏体晶界成网状分布。过共析钢因含有较多的碳、热处理后可得到很高的强度和硬度。通常采用不完全淬火，保留一部分未溶解的渗碳体，淬火后这些渗碳体以粒状分布在马氏体基体内，能提高钢的耐磨性。这种钢多用作工具钢使用。
CAS号：
性质：含碳量高于0.77%的碳素钢。显微组织有珠光体和先析渗碳体。该渗碳体沿原奥氏体晶界成网状分布。过共析钢因含有较多的碳、热处理后可得到很高的强度和硬度。通常采用不完全淬火，保留一部分未溶解的渗碳体，淬火后这些渗碳体以粒状分布在马氏体基体内，能提高钢的耐磨性。这种钢多用作工具钢使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。