2) hydroethyl acrylate
丙烯酸β羟乙酯
1.
For the system of hydroethyl acrylate/butyl acrylate,solution copolymerization were carried out at two sensitive feed monomer composition points by duplicate experiments at 60°C,80°C,100°C,120°C,140°C respectively.
以丙烯酸β羟乙酯(HEA)-丙烯酸正丁酯(BA)共聚体系为研究对象,在共聚单体组成敏感点附近做重复实验,进行了60°C,80°C,100°C,120°C,140°C下的共聚合,用1H-NMR方法测定共聚物的组成,用Mayo-Lewis微分组成方程的误差变量法计算竞聚率,同时给出竞聚率的95%置信区间。
4) 2-hydroxy propylmethacrylate
甲基丙烯酸β羟丙酯
1.
Poly(2-hydroxy propylmethacrylate) (HPMA)/SiO_2 organic-inorganic hybrid material was synthesized in fully transparent homogeneous form.
以甲基丙烯酸β羟丙酯(HPMA)、正硅酸乙酯(TEOS)为原料,基于溶胶凝胶技术合成出聚甲基丙烯酸β羟丙酯PHPMA/SiO2均质透明有机无机杂化材料。
5) β-hydroxypropyl methacrylate
甲基丙烯酸-β-羟丙酯
6) β-hydroxypropyl acrylate
丙烯酸β-羟基丙酯
1.
Chitosan(CS)/poly(N-vinyl-pyrrolidone-co-β-hydroxypropyl acrylate)(NVP-co-β-HPAT) semi-interpenetrating(Semi-IPN) hydrogel(Semi-IPNH) were prepared by incorporating CS into cross-linked poly(NVP-co-β-HPAT) to form a semi-IPN polymeric network.
以壳聚糖(CS),N-乙烯基吡咯烷酮(NVP)和丙烯酸β-羟基丙酯(β-HPAT)为原料,合成了半互穿网络(Semi-IPN)水凝胶P(NVP-co-β-HPAT)/CS(简称Semi-IPNH),其结构经FT-IR,TG和SEM表征。
补充资料:甲基丙烯酸-β-羟丙酯
分子量 144.70
无色透明液体。密度1.066g/cm3(25℃)。 沸点90~93℃(0.933kPa)。 闪点96.7℃(开杯)。折射率1.446(25℃)。在水中有一定的溶解度, 可溶于有机溶剂。易燃,遇明火可引起燃烧。毒性较小。
应用 主要用于制造有活性基团的羟基丙烯酸树脂。涂料工业与环氧树脂、二异氰酸酯、三聚氰胺甲醛树脂等配置,用于制造双组份涂料。油脂工业用作润滑油洗涤的添加剂。纺织工业用于制造织物的胶粘剂,分析化学中用作化学试剂。
无色透明液体。密度1.066g/cm3(25℃)。 沸点90~93℃(0.933kPa)。 闪点96.7℃(开杯)。折射率1.446(25℃)。在水中有一定的溶解度, 可溶于有机溶剂。易燃,遇明火可引起燃烧。毒性较小。
应用 主要用于制造有活性基团的羟基丙烯酸树脂。涂料工业与环氧树脂、二异氰酸酯、三聚氰胺甲醛树脂等配置,用于制造双组份涂料。油脂工业用作润滑油洗涤的添加剂。纺织工业用于制造织物的胶粘剂,分析化学中用作化学试剂。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。