1) refractory carbonaceous gold ore
碳质难处理金矿
1.
A process Ieaching gold from a refractory carbonaceous gold ores with hypochlorous solution was proposed.
论述了碳质金矿的矿物学特性 ,次氯酸钠氯化法直接浸出碳质微细粒浸染型难处理金矿的工艺过程和操作条件 ,讨论了不同因素对浸出过程的影响 ,评述了水溶液氯化法浸取贵州某碳质难处理金矿的试验结
2) arsenic bearing carbon bearing refractory gold concentrate
含砷含碳难处理金精矿
3) refractory gold ore
难处理金矿
1.
Polysulfide leaching of calcine after roasting refractory gold ore by addition of lime;
难处理金矿石加石灰焙烧焙砂的多硫化物浸出
2.
The application status on biohydrometallurgical techniques in the lowgrade copper sulfides,refractory gold ores and other solid mineral resources was reviewed in the paper.
本文总结了国内外生物湿法冶金技术在低品位硫化铜矿、难处理金矿以及其他固体矿产资源中的研究现状,指出了存在的问题,并提出了未来的发展方向。
4) Refractory gold ores
难处理金矿
1.
Current status of studies on bacterial oxidation and pre-disposal of refractory gold ores;
难处理金矿石的细菌氧化预处理研究现状
2.
Current situations of pretreatment method research of the refractory gold ores with as and carbon
含砷含碳双重难处理金矿石预处理方法研究现状
3.
Recent industrial applications of pretreatment of refractory gold ores and concentrates in the world, including roasting, pressure oxidation and bacterial oxidation have been surveyed in this paper.
介绍了国内外难处理金矿预处理技术工业应用现状，这些预处理技术包括：焙烧、加压氧化及细菌氧化。
5) Refractory gold concentrate
难处理金精矿
1.
The current situation of commercial-scale application of the bio-oxidation pretreatment technology of refractory gold concentrate and the analysis of its technological factors;
难处理金精矿生物氧化预处理工艺的工业应用现状及其工艺因素分析
2.
Study on leaching of refractory gold concentrate containing arsenic and sulphur;
某难处理金精矿浸金新工艺试验研究
3.
The gold extraction from refractory gold concentrate on a scale of 20t/d ores treated by technology of fluidized roastingcyanidation along with its running condition are introduced.
介绍了２０ｔ／ｄ规模难处理金精矿沸腾焙烧—氰化提金生产工艺及其运行情况。
6) refractory gold ores
难处理金矿石
1.
Overview of pretreatment technique of refractory gold ores;
难处理金矿石预处理技术综述
2.
Study on technique of oxidation by H 2SO 4 to oxidize refractory gold ores bearing arsenic;
硫酸预氧化难处理金矿石的工艺研究
补充资料：铝碳质整体塞棒
铝碳质整体塞棒
alumina graphite monolithic stopper
IUtanzhi zhengti sa}bdng铝碳质整体塞棒(alumina graphite monoli-thicst叩per)以刚玉和鳞片状石姜为主要原料烧成的控制钢液流量的耐火制品。其特点是整体性好，代替了由传统的袖砖和塞头组装的塞棒，使用更安全，而且还可以通过塞棒向中间罐水口吹氢，净化钢水，防止水口堵塞。 铝碳质整体塞棒的理化指标:A120360%，F·C25%，体积密度2.359/c m3，显气孔率13%，耐压强度14.7MPa，抗折强度(1400℃)5.oMPa，线膨胀率(1000℃)。.5%。其制造工艺是将刚玉、石墨和添加剂等原料按配比称量，以酚醛树脂为结合剂，经混练，用等静压机成型。半成品经干燥后，在无氧化烧成窑内烧成。最后，经X射线无损探伤、车床加工、喷涂防氧化涂层等工序，经检验合格后为成品。铝碳质整体塞棒的工艺流程见图。 刚玉石墨添加剂福猛啮~遍州画画趣画莎甲’ 成品 铝碳质整体塞棒的生产工艺流程 在制造中，配料要准确，原料要符合工艺要求，泥料必须造粒，成型压力为120~150MPa，烧成温度为1000~1350℃。 该制品安装于连铸机中间罐内，用其开启程度来控制钢水流量的大小.要求干燥贮存，使用前必须预热。 (周川生)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。