1) poly(vinyl chloride) supported ferric chloride
聚氯乙烯支载三氯化铁
1.
A variety of aldehydes can be converted into acylals rapidly and conveniently in the presence of catalytic amounts of poly(vinyl chloride) supported ferric chloride reagent (PVC FeCl 3) at room temperature in excellent yields.
聚氯乙烯支载三氯化铁 (PVC FeCl3)试剂在室温条件下能方便快速催化各类醛与乙酸酐反应 ,以良好产率 (75 %～96% )生成相应乙酰缩
2) polystyrene-supported FeCl 3
聚苯乙烯负载三氯化铁
1.
Methods 2% Crosslinked polystyrene-supported FeCl 3 (PS-FeCl 3, 31.
方法各种碳水化合物与丙酮在2%交联聚苯乙烯负载三氯化铁(31。
3) chlorinated polyvinyl chloride-ferric chloride
氯化聚氯乙烯三氯化铁
4) polyvinyl chloride-ferric chloride resin
聚氯乙烯三氯化铁树脂
1.
The preparation method and application as catalyst in the esterification, ester exchange reaction, acetalation (ketalation) and molecular rearrangement reaction of polyvinyl chloride-ferric chloride resin was introduction.
介绍了聚氯乙烯三氯化铁树脂的制备方法和作为催化剂在酯化作用、酯交换作用、缩醛(酮)化作用及分子重排等方面的应用,说明了反应历程。
5) polystyrene-ferric chloride coordination complex
聚苯乙烯-三氯化铁配位化合物
6) EPDM/CPE
三元乙丙胶/氯化聚乙烯
1.
In terms of the blackening of the copper conductor in rubber sheathed cords during production,storage and application,we suggest to use EPDM/CPE system as the insulation and peroxide DCP as the curing agent.
针对传统的橡套软线在加工、储存、使用过程中铜线变色发黑现象,提出绝缘橡皮配方选用三元乙丙胶/氯化聚乙烯(EPDM/CPE)并用体系,采用过氧化物DCP作硫化,这样既解决了橡套软线铜线变色发黑现象,又杜绝了绝缘橡皮发粘、龟裂、脆化等质量问题的发生。
补充资料：聚氯乙烯/氯化聚乙烯共混物
分子式：
CAS号：
性质：系以聚氯乙烯为主，以氯化聚乙烯作冲击改性剂或内增塑剂，配以其他助剂混合而成的多相共混物，所用氯化聚乙烯氯含量为30％～40％，添加量为5％～15％，具有良好的冲击韧性、耐候性及其他综合性能；也存在增塑聚氯乙烯中加入氯含量40％～48％的氯化聚乙烯作永久型增塑剂，改善低温脆性及耐久性。两者均可以机械共混制取，用于各种管材、型材、电线电缆、防水卷材及汽车内饰件等方面。